Zn1+xSb二元体系的相形成和热电性能

在Zn?Sb二元相图固相线以下使Zn和Sb粉末反应并随炉冷却,合成一系列Zn1+xSb(x=0,0.05,0.1,0.15,0.25,0.3)材料,分析Zn–Sb相图中心区域的相形成和热电性能.在此过程中,非化学计量比的混合粉末结晶形成ZnSb和 β-Zn4Sb3相的组合.然后,将材料研磨并热压成致密的ZnSb/β-Zn4Sb3复合材料.X射线衍射、高分辨率透射电镜和电子能量损失谱分析均未发现Sb、Zn元素或其他相.所有材料的热电性能都可以归结为ZnSb和β-Zn4Sb3相的热电行为的结合,并由每种材料中的主相所决定,Zn1.3Sb复合材料具有最好的热电性能.研究发现,Ge掺杂可大幅增加Zn1...

Full description

Saved in:
Bibliographic Details
Published in中国有色金属学报(英文版) Vol. 31; no. 3; pp. 753 - 763
Main Authors Ahmad OSTOVARI MOGHADDAM, Evgeny TROFIMOV, Ting ZHANG, Jordi ARBIOL, Andreu CABOT
Format Journal Article
LanguageChinese
Published Department of Materials Science,Physical and Chemical Properties of Materials,South Ural State University,76 Lenin Ave,Chelyabinsk,454080,Russia%Catalan Institute of Nanoscience and Nanotechnology(ICN2 ,Consejo Superior de Investigaciones Científicas(CSIC)and Barcelona Institute of Science and Technology(BIST),Campus Autonomous University of Barcelona(UAB),Bellaterra,08193 Barcelona,Spain%Catalonia Institute for Energy Research-IREC,Sant Adrià de Besòs,08930 Barcelona,Spain 2021
Catalan Institution for Research and Advanced Studies-ICREA,Pg. Lluís Companys 23,08010 Barcelona,Spain
Subjects
Online AccessGet full text

Cover

Loading…
More Information
Summary:在Zn?Sb二元相图固相线以下使Zn和Sb粉末反应并随炉冷却,合成一系列Zn1+xSb(x=0,0.05,0.1,0.15,0.25,0.3)材料,分析Zn–Sb相图中心区域的相形成和热电性能.在此过程中,非化学计量比的混合粉末结晶形成ZnSb和 β-Zn4Sb3相的组合.然后,将材料研磨并热压成致密的ZnSb/β-Zn4Sb3复合材料.X射线衍射、高分辨率透射电镜和电子能量损失谱分析均未发现Sb、Zn元素或其他相.所有材料的热电性能都可以归结为ZnSb和β-Zn4Sb3相的热电行为的结合,并由每种材料中的主相所决定,Zn1.3Sb复合材料具有最好的热电性能.研究发现,Ge掺杂可大幅增加Zn1.3Sb的Seebeck系数且显著提高其功率因数,540 K时达1.51 mW·m?1·K?2.总之,Zn1.28Ge0.02Sb具有优异、稳定的ZT值,650 K时为1.17.
ISSN:1003-6326
DOI:10.1016/S1003-6326(21)65536-X