Effect of extrinsic pigmentation and surface treatments on biaxial flexure strength after cyclic loading of a translucent ZrO 2 ceramic

• Published in: Dental materials Vol. 35; no. 11; p. 1644
• Main Authors: Bittar, Breno Fortes, Miranda, Jean Soares, Simões, Arthur Chaves, de Carvalho Ramos, Nathália, Machado, João P B, Zhang, Yu, Souza, Rodrigo Othávio Assunção, Leite, Fabíola Pessôa Pereira
• Format: Journal Article
• Language: English
• Published: England 01.11.2019
• Subjects: Ceramics; Flexural Strength; Materials Testing; Pigmentation; Reproducibility of Results; Stress, Mechanical; Surface Properties; Yttrium; Zirconium; Phase transformation; Zirconia surface treatment; Biaxial flexural strength; Surface characterization
• ISSN: 1879-0097

To evaluate the influence of extrinsic pigmentation on the biaxial flexural strength and surface topographic of translucent Y-TZP (InCoris TZI - Sirona - USA) subjected to several surface treatments. Sintered zirconia discs-shaped specimens (n=120) (ø:12mm; thickness:1.2mm; ISO 6872) were prepared and divided (n=15) according to various factors: "extrinsic pigmentation" (n: without; p: with) and "surface treatments" (C: control - as sintered; A: abraded with silica-coated alumina particles (30μm); G: glazed with a thin film of low-fusing porcelain glaze; GH: glazed and etched with 10% hydrofluoridric acid for 60s. Mechanical cycling (1.2×10 cycles, 200N, 3.8Hz) and flexural strength test (1mm/min - 1000kg cell) were performed. Two-way ANOVA and Tukey's were used for statistical test (α=0.05). Weibull analysis was used to evaluate the strength reliability. Samples were analyzed via (1) an optical profilometer to determine the surface roughness (Ra); (2) an X-ray diffraction (XRD) to evaluate phase transformations; and (3) a SEM equipped with an energy dispersive X-ray spectroscopy (EDX) to elucidate morphological properties and chemical compositions. Regardless of the surface treatment (p=0.5459) (Cn: 560.16MPa; Gn: 573.36MPa; An: 643.51MPa; GHn: 542.94MPa; Cp: 628.04MPa; Gp: 641.90MPa; Ap: 554.47MPa; GHp :602.84MPa) and extrinsic pigmentation (p=0.1280) there was no difference in the flexural strength among the experimental groups. According to the XRD analysis, phase transformations occurred in the An group (t→m) and in Ap group (t→c). Surface roughness was affected by surface treatments (An - p=0.001) and extrinsic pigmentation (Gp - p=0.001). The biaxial flexural strength of the tested samples was not affected neither by surface treatments nor by pigmentation, although it can cause phase transformation and promote surface roughness.