Oxide Powder Mixture with Poly-vinyl Alcohol (PVA) and added Polyethylene Glycol (PEG) as Plasticizer

• Published in: Science of sintering Vol. 55; no. 2; pp. 189 - 203
• Main Authors: Labus, Nebojša, Krstić, Jugoslav, Matijašević, Srdjan, Pavlovic, Vladimir
• Format: Journal Article
• Language: English
• Published: Beograd International Institute for the Science of Sintering (IISS) 01.01.2023
• Subjects: Differential thermal analysis; Extensometers; Fourier transforms; Hydrogen bonds; Infrared analysis; Infrared reflection; Infrared spectroscopy; Laminating; Mixed oxides; Plasticizers; Polyethylene glycol; Polymers; Polyvinyl alcohol; Sintering; Solvents; Transmission electron microscopy; Zinc oxide
• ISSN: 0350-820X; 1820-7413
• DOI: 10.2298/SQS220828005L

Сажезак: Смеша прахова саставлена од ZnO, Mn2O3 (MnCO3) и Fe2O3 комбинаци)е прахова )е показивала ламинациу'у током пресовата. Поливинил алкохол (PVA) и комбинаций PVA са полиетилен гликолом (PEG) ко)и )е додат као пластификатор, су уведени као полимерно везиво за пресовате оксидних прахова. Везиво )е уведено тако што )е формирана суспензиу'а смеше различитих оксида прахова у полимерном раствору. Концентрациу'е полимера и састави су варирани. Уклататем растварача добиу'ени су нови матери1али ко)и се састоу'е од честица оксида повезаних полимерима. Ови хибридни материали окарактерисани су методама ометене тоталне рефлексиуе фуриуе трансформисане инфрацрвене спектроскопов (ATR-FTIR) као и диференциуалне термичке анализе (DTA). Микроструктура )е посматрана трансмисоном електронском микроскопном (TEM). Оксид-полимер матери1али су пресовани на притиску од 200 MPa и ширете испреска током греу'ата )е праНено у температурском опсегу од собне до 550°C употребом дилатометра. Наивно je да PVA формира графт полимер са PEG и да посто1и специфична интеракци/а полимера са површином честица оксида.