Electrostatic Beneficiation of Lunar Simulant

Electrostatic beneficiation of lunar regolith is a method allowing refinement of specific minerals in the material for processing on the moon. The use of tribocharging the regolith prior to separation was investigated on the lunar simulant MLS-I by passing the dust through static mixers constructed...

Full description

Saved in:
Bibliographic Details
Published inNASA Center for AeroSpace Information (CASI). Conference Proceedings
Main Authors Trigwell, Steve, Captain, James, Captain, Janine, Arens, Ellen, Quinn, Jacqueline, Calle, Carlos
Format Conference Proceeding
LanguageEnglish
Published Hampton NASA/Langley Research Center 06.06.2006
Subjects
Aluminum
Beneficiation
Charging
Construction materials
Electrostatic shielding
Lunar dust
Lunar environments
Lunar surface
Mineralogy
Mixers
Moon
Organic chemistry
Particle size
Polytetrafluoroethylene
Regolith
Separators
Vacuum chambers
X ray photoelectron spectroscopy
Online AccessGet full text

Cover

More Information
Summary:Electrostatic beneficiation of lunar regolith is a method allowing refinement of specific minerals in the material for processing on the moon. The use of tribocharging the regolith prior to separation was investigated on the lunar simulant MLS-I by passing the dust through static mixers constructed from different materials; aluminum, copper, stainless steel, and polytetrafluoroethylene (PTFE). The amount of charge acquired by the simulant was dependent upon the difference in the work function of the dust and the charging material. XPS and SEM were used to characterize the simulant after it was sieved into five size fractions (> 100 pm, 75-100 pm, 50- 75 pm, 50-25 pm, and < 25 pm), where very little difference in surface composition was observed between the sizes. Samples of the smallest (< 25 pm) and largest (> 100 pm) size fractions were beneficiated through a charge separator using the aluminum (charged the simulant negatively) and PTFE (charged positively) mixers. The mass fractions of the separated simulant revealed that for the larger particle size, significant unipolar charging was observed for both mixers, whereas for the smaller particle sizes, more bipolar charging was observed, probably due to the finer simulant adhering to the inside of the mixers shielding the dust from the charging material. Subsequent XPS analysis of the beneficiated fractions showed the larger particle size fraction having some species differentiation, but very little difference for the smaller.size. Although MLS-1 was made to have similar chemistry to actual lunar dust, its mineralogy is quite different. On-going experiments are using NASA JSC-1 lunar simulant. A vacuum chamber has been constructed, and future experiments are planned in a simulated lunar environment.