Oxygen potentials, oxygen diffusion coefficients and defect equilibria of nonstoichiometric (U,Pu)O^sub 2±x
Oxygen potential of (U,Pu)O2±x was evaluated based on defect chemistry using an updated experimental data set. The relationship between oxygen partial pressure and deviation x in (U,Pu)O2±x was analyzed, and equilibrium constants of defect formation were determined as functions of Pu content and tem...
Saved in:
Published in | Journal of nuclear materials Vol. 486; p. 424 |
---|---|
Main Authors | , , , , |
Format | Journal Article |
Language | English |
Published |
Amsterdam
Elsevier BV
01.04.2017
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Oxygen potential of (U,Pu)O2±x was evaluated based on defect chemistry using an updated experimental data set. The relationship between oxygen partial pressure and deviation x in (U,Pu)O2±x was analyzed, and equilibrium constants of defect formation were determined as functions of Pu content and tem- perature. Brouwer's diagrams were constructed using the determined equilibrium constants, and a relational equation to determine O/M ratio was derived as functions of Of M ratio, Pu content and temperature. In addition, relationship between oxygen potential and oxygen diffusion coefficients were described. |
---|---|
ISSN: | 0022-3115 1873-4820 |