Effects of Cr^sub 2^O^sub 3^ addition on the phase, mechanical properties, and microstructure of zirconia-toughened alumina added with TiO^sub 2^ (ZTA–TiO^sub 2^) ceramic composite

Increasing demand for stronger cutting tools has led to the development of several novel composites and other multi-phase ceramics with better properties, particularly high fracture toughness. Cr2O3 is used as new material additive in this study, as it has attracted attention due to the formation of...

Full description

Saved in:
Bibliographic Details
Published inInternational journal of refractory metals & hard materials Vol. 61; p. 40
Main Authors Manshor, Hanisah, Azhar, Ahmad Zahirani, Rashid, Rashita Abd, Sulaiman, Shazreen, Abdullah, Ezzat Chan, Ahmad, Zainal Arifin
Format Journal Article
LanguageEnglish
Published Shrewsbury Elsevier BV 01.12.2016
Subjects
Aluminum oxide
Ceramic tools
Ceramics
Chromium oxides
Crack propagation
Cutting parameters
Cutting tool materials
Effects
Fracture mechanics
Fracture toughness
Mechanical properties
Microstructural analysis
Microstructure
Physical properties
Sintering
Studies
Titanium oxides
Zirconia toughened alumina
Zirconium dioxide
Online AccessGet full text

Cover

More Information
Summary:Increasing demand for stronger cutting tools has led to the development of several novel composites and other multi-phase ceramics with better properties, particularly high fracture toughness. Cr2O3 is used as new material additive in this study, as it has attracted attention due to the formation of isovalent solid solution when added to Al2O3, contributing to improved fracture toughness. Thus, the aim of this study is to investigate the effects of the addition of Cr2O3 at a concentration of between 0.0 wt% to 1.0 wt% on the physical properties, microstructural features and phase of a ZTA-TiO2 ceramics composite. The samples were prepared by wet-mixing and uniaxial compaction, then sintered for 1 h at 1600 °C under pressureless conditions. The sintered samples were then identified in terms of their density, hardness, fracture toughness and crack propagation, and were then subjected to microstructural analysis by XRD and FESEM. It was discovered that with addition of 0.6 wt% of Cr2O3 to the composite, an optimum density of 4.0630 g/cm3, hardness of 1681 HV, and fracture toughness of 7.15 MPa.m1/2 were obtained. As a result of this addition, plate-like Al2O3 grains were observed, which caused cracks formed in the composite to spread in an inter-granular manner. This confirmed that the properties of ZTA-TiO2 ceramics composite were augmented by the addition of 0.6 wt% Cr2O3.