Preparation of PbS Quantum Dots on TiO^sub 2^ Porous Film by an In-Situ Process for Solar Cells Application
PbS QDs with size of 7-9 nm were deposited by an in-situ room temperature solution chemical reaction process using lead nitrate cationic resource in a form of solid precursor film and ammonium sulfide as an anionic reaction solution. The TiO... film with PbS QDs deposited by the in-situ method was u...
Saved in:
Published in | Integrated ferroelectrics Vol. 164; no. 1; p. 6 |
---|---|
Main Authors | , , , , |
Format | Journal Article |
Language | English |
Published |
Philadelphia
Taylor & Francis Ltd
01.01.2015
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | PbS QDs with size of 7-9 nm were deposited by an in-situ room temperature solution chemical reaction process using lead nitrate cationic resource in a form of solid precursor film and ammonium sulfide as an anionic reaction solution. The TiO... film with PbS QDs deposited by the in-situ method was used to fabricate QDs-sensitized solar cells. The power conversation efficiency of the as prepared solar cells improved by increasing cycle numbers. For 7 deposition cycles of PbS QDs, the PbS/TiO... device shows an open-circuit voltage (Voc) of 538 mV, a short-circuit current density (Jsc) of 0.145 mA, fill factor (FF) of 0.416 and a power conversion efficiency (...) of 0.163%. (ProQuest: ... denotes formulae/symbols omitted.) |
---|---|
ISSN: | 1058-4587 1607-8489 |