COMPARISON OF THE MICROSTRUCTURE OF WELD METALS IN WELDED JOINTS MADE WITH RUTILE ELECTRODES BASED ON DOMESTIC RAW MATERIALS AND ELECTRODES OF A WELL-KNOWN MANUFACTURER

This paper presents the results of comparative testing of the quality of the weld metal of welded plates of low carbon non alloyed steel using rutile type coated electrodes produced in IHIS and electrodes JADRAN-S produced in Jesenice. The aim was to master the technological process of producing ele...

Full description

Saved in:
Bibliographic Details
Published inAnnals of Faculty Engineering Hunedoara Vol. 13; no. 2; p. 75
Main Authors Mrdak, Mihailo, Bajic, Nikola, Rakin, Marko, Stojadinovic, Slobodan, Veljic, Darko
Format Journal Article
LanguageEnglish
Published Hunedoara Faculty of Engineering Hunedoara 01.04.2015
Subjects
Electrodes
Welding
Wire
Online AccessGet full text

Cover

More Information
Summary:This paper presents the results of comparative testing of the quality of the weld metal of welded plates of low carbon non alloyed steel using rutile type coated electrodes produced in IHIS and electrodes JADRAN-S produced in Jesenice. The aim was to master the technological process of producing electrodes coated with a rutile coating based on domestic raw materials. For experimental testing used was an electrode with a medium thick rutile coating with a core of solid wire Ø 2.0 mm in diameter marked IHIS E 35 R. Based on comparative analysis of the weld metal test results of welded joints made with electrodes produced in IHIS in relation to the electrodes of the well known manufacturer the appropriate conclusions are given.
ISSN:1584-2665
2601-2332