Effect of Dentin Bonding Agent Acidity on Surface Microhardness of Mineral Trioxide Aggregate
Purpose: This study investigated the effect of dentin bonding agent acidity on surface microhardness of MTA. Materials and Methods: Forty cylindrical molds (3 mm×5 mm) were prepared, and three dentin bonding agents with different acidities: Adper Single Bond 2 (ASB), Single Bond Universal (SBU), and...
Saved in:
Published in | Journal of Korean dental science Vol. 17; no. 1; pp. 36 - 44 |
---|---|
Main Authors | , |
Format | Journal Article |
Language | Korean |
Published |
2024
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Purpose: This study investigated the effect of dentin bonding agent acidity on surface microhardness of MTA. Materials and Methods: Forty cylindrical molds (3 mm×5 mm) were prepared, and three dentin bonding agents with different acidities: Adper Single Bond 2 (ASB), Single Bond Universal (SBU), and Clearfil SE bond 2 (CSE) were applied to the inner surface of the molds (n=10). No bonding agent was applied in the control group. MTA was mixed and inserted into the molds and sealed with a wet cotton pellet for 4 days. After setting, the Vickers microhardness (HV) test was done at 200, 400, 600 ㎛ from the inner surface of the mold. One-way ANOVA was conducted for all samples. A P-value of less than .05 was considered significant. Tukey HSD test was performed for post-hoc analysis. Results: The mean HV values and standard deviations were 67.02±11.38 (Con), 48.76±11.33 (ASB), 43.78±11.19 (CSE), 37.84±9.36 (SBU), respectively. The difference between the control group and the experimental groups was statistically significant (P<0.001). The difference between ASB and SBU was statistically significant (P<0.001), while the difference between SBU and CSE was not. There were no statistically significant differences between the various points from the inner surface of the mold within each group (P>0.05). Conclusion: Results of the current study indicate that use of dentin bonding agents with MTA can reduce the surface microhardness of MTA. Moreover, there is a direct relationship between the acidity of dentin bonding agents and the surface microhardness of MTA. |
---|---|
Bibliography: | KISTI1.1003/JNL.JAKO202409443284787 |
ISSN: | 2005-4742 2713-7651 |