TiN Ion-Plating이 교정용 브라켓의 접착강도에 미치는 영향

• Published in: Korean journal of orthodontics Vol. 27; no. 1; pp. 157 - 171
• Main Authors: 김석용, 권오원, 김교한, KIM, Seok-Yong, KWON, Oh-Won, KIM, Kyo-Han
• Format: Journal Article
• Language: Korean
• Published: 1997
• ISSN: 1225-5610; 2005-372X

This study was conducted to see the effect of TiN ion-plating on the bond strength of orthodontic bracket. Three stainless-steel brackets with different base types were chosen; when TiN ion-plated brackets and non iorrplated brackets were bonded to the teeth, initial and long-term bond strength were measured, The observations oi bonding surface and failure sites through the scanning electron microscope were analysed and compared. The summary of this study was as follows; ${\cdot}$ When TiN ion-plating was not applied, the Micro-Loc type was the highest in bond strength atter 24 hours as $5.89{\pm}1.77$ MPa, followed by $4,27{\pm}1.12MPa$ for Foil Mesh type and $2.64{\pm}0.58MPa$ for Undercut type(P<0.05). ${\cdot}$ Under TiN ion-plating, the bond strength after 24 hours showed: Micro-Loc type $-6.26{\pm}1.51MPa$, Foil Mesh type $-7.45{\pm}2.01MPa$, Undercut type $-2.93{\pm}0.84MPa$. Unlike in the case of non ion-plating, Foil Mesh type showed a higher strength than Micro-Loc type, with Undercut type still showing the lowest bond strength(P<0.05). The bond strength, after 24 hours, increased in case of ion-plated in all 3 types, but a significant increase was shown only in Foil Mesh type(P<0.001). ${\cdot}$ Under a long-term immersion, regardless of ion or non ion-plating, bond strength in general increased over the initial bond strength(one day), with more stability. ${\cdot}$ Through scanning electron microscopic observation of bonding surface, it was found that, regardless of the bracket base type or the application of ion-plating, the resin was thoroughly spreaded into bracket base to form a solid bonding surface between the bracket and the tooth. This was also true in case of a long-term immersion. ${\cdot}$ The scanning electron microscopic observation of failure sites revealed diverse failure patterns. TiN ion-plating이 교정용 브라켓의 접착강도에 미치는 영향을 알아보기 위하여 세 종류의 서로 다른 기저면형태를 가지는 스테인레스 스틸제의 브라켓을 선택하고, TiN ion-plating 된 브라켓과 ion-plating 되지 않은 브라켓을 치아에 접착시켰을 때 초기 및 장기접착강도, 접착계면의 주사전자현미경 관찰, 파단면의 주사전자현미경 관찰을 비교 분석하여 다음과 같은 결론을 얻었다. ${\cdot}$ TiN ion-plating을 하지 않은 경우 24 시간 후의 접착강도는 Micro-Loc형이 $5.89{\pm}1.77MPa$, Foil Mesh형이 $4.27{\pm}1.12MPa$, Undercut형이 $2.64{\pm}0.58MPa$로 Micro-Loc형 이 가장 높았고, 그 다음이 Foil Mesh형 그리고 Undercut 형의 순으로 나타났다(P<0.05). ${\cdot}$ TiN ion-plating시 24시간 투의 접착강도는 Micro-Loc형이 $6.26{\pm}1.51MPa$, Foil Mesh형이 $7.45{\pm}2.01MPa$, Undercut형 이 $2.93{\pm}0.84 MPa$로 ion-plating 하지 않은 경우와 달리 Foil Mesh형이 Micro-Loc형보다 오히려 높게 나타났고, Undercut형이 역시 가장 낮은 접착강도를 나타내었다(P<0.05). Ion-plating 유무에 따른 24시간 후의 접착강도는 3가지형 모두에서 ion-plating시 증가하였으나 Foil Mesh형에서만 유의한 증가가 있었다(P<0.001). ${\cdot}$ 장기침적시 ion-plaling의 유무에 관계없이 전반적으로 초기(1일)접착강도보다 증가하였으며 접착력의 안정성을 나타내었다. ${\cdot}$ 접착계면의 주사전자현미경 관찰 결과 브라켓 기저면의 형태나 ion-plating 유무에 관계 없이 레진이 브라켓 기저면으로 잘 퍼져들어가 브라켓과 치아와의 사이에 견고한 접착면을 나타내었고, 장기침적의 경우도 같은 양상을 나타내었다. ${\cdot}$ 파단면의 주사전자현미경 관찰에서는 다양한 파괴 양상이 나타났다.