TiN 코팅된 SKD11과 SKD61의 내마모 성질레 미치는 이온주입 효과

• Published in: 한국표면공학회지 Vol. 30; no. 6; pp. 391 - 399
• Main Authors: 장태석, 이수완, 문대원, 방건웅
• Format: Journal Article
• Language: Korean
• Published: 1997
• ISSN: 1225-8024

To figure out wheher the tribological properties of a hras-coating layer can be imporved by ion implantatio, TiN-coated SKD 11 61 were implanted with nitrogen ion and their wear peoperties were examined systematically. The amount of nitrgen ione implanted on the coating layer was $2 \times 10^{15},\;10^{16},\;10^{17},\;and\;10^{18}\;ions/\textrm{cm}^2$, respectively. X-ray diffraction revealed theintensity of the peaks belong TiN tended to increase as the ion dose increased, which implied that the implantation promoted the formation of TiN in the coated later. Howeverthe hardensity of the specimens increased then decreased again as the ion dose increased, resulting in a obvious drop of the hardness for the ion does of $2 \times 10^{18}\;ions/\textrm{cm}^2$<\. While the adhesion of the coated layer of SKD 61 was excllent regrdless of the implatation, the adhesion of the later of SKD 11 was apparently improved by the implantation. The overall wear properties of SKD 11 was better than that of SKD 61, and the best result was yielded at the ion dose of $2 \times 10^{15}\;ions/\textrm{cm}^2$<\.