Performance of a Pd-Zn Cathode Electrode in a H[sub.2] Fueled Single PEM Fuel Cell

• Published in: Electronics (Basel) Vol. 11; no. 17
• Main Authors: Bampos, Georgios, Bebelis, Symeon
• Format: Journal Article
• Language: English
• Published: MDPI AG 01.09.2022
• Subjects: Design and construction; Electrodes; Materials; Palladium; Greece
• ISSN: 2079-9292; 2079-9292
• DOI: 10.3390/electronics11172776

A 21.7 wt.% Pd—7.3 wt.% Zn/C electrocatalyst prepared via the wet impregnation (w.i.) method was deposited onto commercial carbon cloth (E-TEK) and tested towards its electrocatalytic performance as a cathode electrode material for oxygen reduction reaction (ORR) in a H[sub.2] fueled single proton-exchange membrane fuel cell (PEMFC). A commercial PtRu electrode (E-TEK) was used as PEM anode for hydrogen oxidation reaction (HOR). The performance of the aforementioned PEMFC was compared with that of the same PEMFC with two different Pt-based cathodes, which were prepared by deposition onto commercial carbon cloth (E-TEK) of 29 wt.% Pt/C synthesized via w.i. and of commercial 29 wt.% Pt/C (TKK). The metal loading of the tested cathode electrodes was 0.5 mg[sub.met] cm[sup.−2] . Comparison was based both on polarization curves and on electrochemical impedance spectroscopy (EIS) measurements at varying cell potential. In terms of power density, the lowest and highest performance was exhibited by the PEMFC with the 21.7 wt.% Pd—7.3 wt.% Zn/C cathode and the PEMFC with the commercial 29 wt.% Pt/C (TKK) cathode electrode, respectively. This behavior was in accordance with the results of EIS measurements, which showed that the PEMFC with the 21.7 wt.% Pd—7.3 wt.% Zn/C cathode exhibited the highest polarization resistance.