STYRENE-ISOPRENE-STYRENE TRI BLOCK COPOLYMERS WITH ADAPTED DIBLOCK COPOLYMERS

• Main Authors: DE KEYZER, NOEL, RAYMOND, MAURICE, MENSEN-VEURINK, JACQUELINE, MARGARETHA, VAN DE VLIET, BIRGITTE, MARIA, LUDOVICA, CHRISTINE, GERARD, ERIC-JACK
• Format: Patent
• Language: English; French
• Published: 23.10.1997
• Edition: 6
• Subjects: ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; ADHESIVES; CHEMISTRY; CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION ORPROCESSING OF GOODS; COMPOSITIONS BASED THEREON; COMPOSITIONS OF MACROMOLECULAR COMPOUNDS; DYES; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; METALLURGY; MISCELLANEOUS APPLICATIONS OF MATERIALS; MISCELLANEOUS COMPOSITIONS; NATURAL RESINS; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ORGANIC MACROMOLECULAR COMPOUNDS; PAINTS; POLISHES; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS; TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINSTCLIMATE CHANGE; THEIR PREPARATION OR CHEMICAL WORKING-UP; USE OF MATERIALS AS ADHESIVES

Hot melt adhesive compositions comprising: (a,1) from 75-90 parts by weight of a triblock copolymer A1B1A2 where A1 and A2 represent predominantly poly(monovinyl aromatic) blocks of the same or different peak molecular weight in the range of from 5,000 to 20,000 g/mol, wherein B1 represents a predominantly poly(isoprene) block while the average apparent molecular weight of the total triblock copolymer is in the range of from 160,000 to 250,000 g/mol, and the monovinyl aromatic monomer content is in the range of from 15 to 25 wt.%; (a,2) from 10 to 25 parts by weight of a diblock copolymer A3B2, wherein A3 represents a predominantly poly(monovinyl aromatic) block having a peak molecular weight in the range of from 5,000 to 20,000 g/mol, and wherein B2 represents a poly(isoprene) block having an average apparent molecular weight calculated from GPC measurements which is from 80 to 110 % of the average molecular weight calculated from GPC measurements of block B1, and wherein the monovinyl aromatic monomer content is in the range of from 5 to 17 %; (b) from 50 to 400 parts by weight of a tackifying resin; (c) from 0 to 100 parts by weight of a plasticiser and/or softening agent. L'invention concerne des compositions adhésives à l'état fondu, qui comprennent: (a, 1) de 75 à 90 parties en poids d'un copolymère triséquencé A1B1A2, dans lequel A1 et A2 représentent des séquences principalement poly(monovinyle aromatique) de poids moléculaires maximum égaux ou différents, variant entre 5000 et 20000 g/mol; B1 représente une séquence principalement poly(isoprène), le poids moléculaire apparent moyen du copolymère triséquencé total se situant entre 160000 et 250000 g/mol et la teneur en monomère aromatique monovinyle variant entre 15 et 25 % en poids; (a, 2) de 10 à 25 parties en poids d'un copolymère diséquencé A3B2, dans lequel A3 représente une séquence principalement poly(monovinyle aromatique) de poids moléculaire maximum allant de 5000 à 20000 g/mol, et B2 représente une séquence poly(isoprène) dont le poids moléculaire apparent moyen, calculé à partir de mesures effectuées par GPC, varie entre 80 et 110 % du poids moléculaire moyen calculé à partir de mesures effectuées par GPC de la séquence B1, la teneur en monomère aromatique monovinyle variant entre 5 et 17 %; (b) de 50 à 400 parties en poids d'une résine adhésive; (c) de 0 à 100 parties en poids d'un agent plastifiant et/ou adoucissant.