HOT-ROLLED STEEL SHEET AND METHOD FOR MANUFACTURING SAME

• Main Authors: YOKOI Tatsuo, KAI Shinsuke, HAYASHIDA Teruki, ANDO Jun, SHUTO Hiroshi, SAKAKIBARA Mutsumi
• Format: Patent
• Language: English; French; Japanese
• Published: 17.09.2020
• Subjects: ALLOYS; CHEMISTRY; FERROUS OR NON-FERROUS ALLOYS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS; METALLURGY; METALLURGY OF IRON; MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; TREATMENT OF ALLOYS OR NON-FERROUS METALS

A hot-rolled steel sheet has a specified chemical composition, wherein, when the thickness of the steel sheet is defined as "t", a metallographic structure lying between a surface of the steel sheet and a depth t/4 from the surface in the steel sheet contains tempered martensite and/or lower bainite in a total volume fraction of 90% or more, the tensile strength is 980 MPa or more, and the average Ni concentration in the surface is 7.0% or more. L'invention concerne une tôle d'acier laminée à chaud qui a une composition chimique spécifiée. Lorsque l'épaisseur de la tôle d'acier est définie comme étant « t », une structure métallographique se trouvant entre une surface de la tôle d'acier et une profondeur de t/4 à partir de la surface dans la tôle d'acier contient de la martensite revenue et/ou de la bainite inférieure en une fraction volumique totale supérieure ou égale à 90 %. La résistance à la traction de la tôle d'acier est supérieure ou égale à 980 MPa et la concentration moyenne de Ni dans sa surface est supérieure ou égale à 7,0 %. この熱延鋼板は、所定の化学組成を有し、厚さをｔとしたとき、表面からｔ／４の位置における金属組織が、焼き戻しマルテンサイト及び下部ベイナイトのいずれか一方あるいは両方を、体積率の合計で９０％以上含有し、引張強さが９８０ＭＰａ以上であり、前記表面における平均Ｎｉ濃度が７．０％以上である。