FLAME RETARDANT POLYISOCYANURATE FOAM

• Main Authors: KASHIWAMOTO, Yuudai, YAMAMOTO, Shigeo
• Format: Patent
• Language: English; French
• Published: 27.06.2019
• Subjects: AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F,C08G; CHEMISTRY; COMPOSITIONS BASED THEREON; GENERAL PROCESSES OF COMPOUNDING; MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONSONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS; METALLURGY; ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES ASCOMPOUNDING INGREDIENTS; WORKING-UP

An object of the present invention is to provide a polyisocyanurate foam having excellent flame retardancy and a heat insulator and building material comprising the same. An object of the present invention is to provide a polyisocyanurate foam having excellent flame retardancy and a heat insulator and building material comprising the same. A flame retardant polyisocyanurate foam produced by curing a mixture comprising a polyol (A), a surfactant (B), a catalyst (C), a blowing agent (D), a polyisocyanate (E) and a flame retardant (F), wherein the catalyst (C) comprises a trimerization catalyst; the water content in the blowing agent (D) is less than 0.2 parts by mass based on 100 parts by mass of the total of the polyol (A) and the polyisocyanate (E); the flame retardant (F) comprises a red phosphorus-based flame retardant and aluminum hydroxide, and the volume average diameter of the aluminum hydroxide is not less than 40 µm when measured by laser diffractometry; the total content of the red phosphorus-based flame retardant and the aluminum hydroxide is 6 to 36 parts by mass based on 100 parts by mass of the total of the polyol (A) and the polyisocyanate (E); and the equivalent ratio of an isocyanate group in the polyisocyanate (E) to the total active hydrogen groups contained in the polyol (A), the surfactant (B), the catalyst (C) and the blowing agent (D) (NCO/OH ratio) is more than 2.0. L'invention a pour objet de produire une mousse de polyisocyanurate ayant une excellente ininflammabilité, et un isolant thermique et un matériau de construction comprenant cette mousse. L'invention concerne une mousse de polyisocyanurate ignifuge produite par durcissement d'un mélange comprenant un polyol (A), un tensioactif (B), un catalyseur (C), un agent gonflant (D), un polyisocyanate (E) et un ignifugeant (F), le catalyseur (C) comprenant un catalyseur de trimérisation; la teneur en eau de l'agent gonflant (D) est inférieure à 0,2 partie en masse sur la base de 100 parties en masse du total du polyol (A) et du polyisocyanate (E). L'ignifugeant (F) comprend un ignifugeant à base de phosphore rouge et d'hydroxyde d'aluminium, et le diamètre moyen en volume de l'hydroxyde d'aluminium n'est pas inférieur à 40 µm lorsqu'il est mesuré par diffractométrie laser. La teneur totale de l'ignifugeant à base de phosphore rouge et d'hydroxyde d'aluminium est de 6 à 36 parties en masse sur la base de 100 parties en masse du total du polyol (A) et du polyisocyanate (E). Le rapport équivalent d'un groupe isocyanate dans le polyisocyanate (E) aux groupes hydrogène actifs totaux présents dans le polyol (A), le tensioactif (B), le catalyseur (C) et l'agent gonflant (D) (rapport NCO/OH) est supérieur à 2,0.