HIGH-STRENGTH THIN STEEL SHEET AND METHOD FOR MANUFACTURING SAME

• Main Authors: TOYODA, Shunsuke, KIZU, Taro, KIDO, Akimasa, TADANI, Tetsushi
• Format: Patent
• Language: English; French; Japanese
• Published: 12.01.2017
• Subjects: ALLOYS; CHEMISTRY; FERROUS OR NON-FERROUS ALLOYS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS; MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL; METALLURGY; METALLURGY OF IRON; MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; PERFORMING OPERATIONS; PUNCHING METAL; ROLLING OF METAL; TRANSPORTING; TREATMENT OF ALLOYS OR NON-FERROUS METALS

The present invention is configured so as to have a predetermined composition, a carbon content equivalent value C* of the total amount of Ti, Nb, and V deposits having a grain size of less than 20 nm of 0.010-0.100% by mass, a Fe content of 0.03-0.50% by mass in Fe deposits, and an average grain size of (4000/TS)2 µm or less (where TS is tensile strength (MPa)) of ferrite grains having the top 5% largest grain size in the ferrite grain size distribution of a cross section in the rolling direction. La présente invention est conçue de façon à obtenir une composition prédéterminée, une valeur de teneur en carbone équivalente C*, due à la quantité totale des dépôts de Ti, Nb et V de taille de grain inférieure à 20 nm, de 0,010 à 0,100 % en masse, une teneur en Fe de 0,03 à 0,50 % en masse dans les dépôts de Fe et une taille de grain moyenne inférieure ou égale à (4000/TS)2 µm (où TS est la résistance à la traction (MPa)) pour les 5 % des grains de ferrite les plus grands dans la distribution de taille des grains de ferrite d'une section transversale dans la direction de laminage. 所定の組成とし、粒径が20nm未満のTi、NbおよびV析出物の合計の炭素量換算値C*を0.010～0.100質量％とし、また、Fe析出物中におけるFe量を0.03～0.50質量％とし、さらに、圧延方向断面のフェライト粒径分布において、粒径の大きい上位5％のフェライト粒の平均粒径を、(4000/TS)2μm以下（TSは引張強度（MPa））とする。