GLUING SUBSTRATES TOGETHER BY MEANS OF A SINGLE-COMPONENT POLYURETHANE ADHESIVE

• Main Authors: SEBESTIAN, MILAN, KOLENDA, FELICITAS
• Format: Patent
• Language: English; French; German
• Published: 14.11.2013
• Subjects: ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; ADHESIVES; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F,C08G; CHEMISTRY; COMPOSITIONS BASED THEREON; DYES; GENERAL PROCESSES OF COMPOUNDING; MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONSONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS; METALLURGY; MISCELLANEOUS APPLICATIONS OF MATERIALS; MISCELLANEOUS COMPOSITIONS; NATURAL RESINS; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ORGANIC MACROMOLECULAR COMPOUNDS; PAINTS; POLISHES; THEIR PREPARATION OR CHEMICAL WORKING-UP; USE OF MATERIALS AS ADHESIVES; WORKING-UP

Verfahren zum Verkleben von Substraten, umfassend mindestens die Schritte - Aufbringen eines Einkomponenten-Polyurethanklebers auf mindestens eines der zu verklebenden Substrate, wobei der Einkomponenten-Polyurethankleber mindestens ein Treibmittel, ausgewählt aus Dimethylether, 1,1-Difluorethan (R 152a) und Dimethoxymethan (Methylal) enthält, und aus einem Druckbehälter in Form eines Schaums appliziert wird, und anschließendes Zusammendrücken der zu verklebenden Substrate, sowie Einkomponenten-Polyurethankleber zur Verwendung in diesem Verfahren, enthaltend - 30 bis 70 Gew.-% mindestens einer Verbindung mit zwei oder mehreren, gegebenenfalls verkappten, Isocyanat-Gruppen, - 20 bis 60 Gew.-% mindestens einer Verbindung, die mindestens zwei Hydroxygruppen aufweist, - 0,01 bis 2,5 Gew.-%, mindestens eines Härtungskatalysators, - 5 bis 49,99 Gew.-%, mindestens eines Treibmittels, und - 0 bis 10 Gew.-% mindestens eines Schaumstabilisators, jeweils bezogen auf das Gesamtgewicht des Einkomponenten-Polyurethanklebers, wobei der Anteil an Dimethylether, 1,1-Difluorethan und Dimethoxymethan, bezogen auf die Gesamtmenge enthaltener Treibmittel, mindestens 50 Gew.-% beträgt. The invention relates to a method for gluing substrates together, comprising at least the following steps: applying a single-component polyurethane adhesive to at least one of the substrates to be glued together, wherein the single-component polyurethane adhesive contains at least one blowing agent selected from dimethyl ether, 1,1-difluoroethane (R 152a) and dimethoxymethane (methylal) and is applied from a pressurized container in the form of a foam; and subsequently pressing together the substrates to be glued together. The invention further relates to a single-component polyurethane adhesive for use in said method, containing 30 to 70 wt% of at least one compound having two or more, optionally blocked, isocyanate groups, 20 to 60 wt% of at least one compound comprising at least two hydroxy groups, 0.01 to 2.5 wt% of at least one hardening catalyst, 5 to 49.99 wt% of at least one blowing agent, and 0 to 10 wt% of at least one foam stabilizer, each based on the total weight of the single-component polyurethane adhesive, wherein the content of dimethyl ether, 1,1-difluoroethane and dimethoxymethane is at least 50 wt% based on the total quantity of blowing agents that are present. L'invention concerne un procédé pour le collage de substrats comprenant au moins les étapes consistant : à appliquer une colle polyuréthane monocomposant sur au moins l'un des substrats à coller. La colle polyuréthane monocomposant contient au moins un agent d'expansion, choisi parmi l'éther diméthylique, le 1,1-difluoroéthane (R 152a) et le diméthoxyméthane (méthylal), et est appliquée à partir d'un récipient sous pression sous la forme d'une mousse; et à presser ensuite les substrats à coller l'un contre l'autre. L'invention concerne également une colle polyuréthane monocomposant destinée à être utilisée dans ledit procédé, contenant : - de 30 à 70 % en poids d'au moins un composé comprenant deux groupes isocyanate éventuellement coiffés ou plus; - de 20 à 60 % en poids d'au moins un composé qui comprend au moins deux groupes hydroxy; - de 0,01 à 2,5 % en poids d'au moins un catalyseur de durcissement; - de 5 à 49,99 % en poids d'au moins un agent d'expansion; et - de 0 à 10 % en poids d'au moins un stabilisateur de mousse, respectivement rapporté au poids total de la colle polyuréthane monocomposant, la proportion en éther diméthylique, en 1,1-difluoroéthane et en diméthoxyméthane, rapporté à la quantité totale d'agent d'expansion contenu, atteignant au moins 50 % en poids.