HOT ROLLED STEEL SHEET, COLD ROLLED STEEL SHEET AND PROCESS FOR PRODUCING THE SAME

• Main Authors: YASUYAMA, MASANORI, NISHIBATA, HITOMI, TOMIDA, TOSHIROU, IMAI, NORIO, KAWANO, KAORI, TOKI, TAMOTSU, WAKITA, MASAYUKI, YOSHIDA, MITSURU
• Format: Patent
• Language: English; French; Japanese
• Published: 08.02.2007
• Subjects: ALLOYS; CHEMICAL SURFACE TREATMENT; CHEMISTRY; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATIONOR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY IONIMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; COATING MATERIAL WITH METALLIC MATERIAL; COATING METALLIC MATERIAL; DIFFUSION TREATMENT OF METALLIC MATERIAL; FERROUS OR NON-FERROUS ALLOYS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION INGENERAL; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS; MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVINGMATERIAL; METALLURGY; METALLURGY OF IRON; MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; PERFORMING OPERATIONS; PUNCHING METAL; ROLLING OF METAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THESURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; TRANSPORTING; TREATMENT OF ALLOYS OR NON-FERROUS METALS

[PROBLEMS] To provide a steel sheet excelling in mechanical strength, processability and thermal stability that is suitable as a material for use in automobiles, home electric appliances, mechanical structures, architecture, etc. and provide a process for producing the same. [MEANS FOR SOLVING PROBLEMS] There is provided a steel sheet of low-alloy steel or carbon steel whose main phase consists of ferrite, wherein the average crystal grain diameter of ferrite at a position of depth corresponding to 1/4 of the sheet thickness from the steel sheet surface, D µm, satisfies the following formulae (1) and (2), and wherein the rate of increase at 700°C of average crystal grain diameter of ferrite at a position of depth corresponding to 1/4 of the sheet thickness from the steel sheet surface, X µm/min, and the above average crystal grain diameter D satisfy the following formula (3). D(µm) = 7 (1) D = 2.7+5000/(5+350·C+40·Mn)2 (2) D·X = 0.1 (3) Le problème à résoudre dans le cadre de cette invention concerne l'obtention d'une feuille d'acier possédant d'excellentes propriétés de résistance mécanique, d'aptitude au traitement et de stabilité thermique, qui est appropriée en tant que matériau utilisé dans les automobiles, les appareils électroménagers, les structures mécaniques, l'architecture, etc. ; ainsi qu'un procédé de production correspondant. La solution proposée consiste à produire une feuille d'acier composée d'un acier faiblement allié ou d'un acier au carbone dont la phase principale comprend de la ferrite, le diamètre moyen d'un grain de cristal d'une ferrite à une profondeur de position correspondant à 1/4 de l'épaisseur de la feuille depuis la surface de la feuille d'acier, D µm, satisfait les formules suivantes (1) et (2), et le taux de croissance à 700 °C du diamètre moyen d'un grain de cristal d'une ferrite à une profondeur de position correspondant à 1/4 de l'épaisseur de la feuille depuis la surface de la feuille d'acier, X µm/min, et le diamètre moyen D de grain de cristal satisfont la formule suivante (3). D(µm) = 7 (1) D = 2.7+5000/(5+350·C+40·Mn)2 (2) D·X = 0.1 (3)