MULTILAYERED FILM MADE OF (METH)ACRYLATE COPOLYMER AND POLYCARBONATE

• Main Authors: WICKER, MICHAEL, RUEPPEL, MONA, DASSINGER, GABRIELE, REINHEIMER, ERIC, SCHULTES, KLAUS, ALBRECHT, KLAUS
• Format: Patent
• Language: English; French; German
• Published: 09.06.2005
• Edition: 7
• Subjects: CHEMISTRY; COMPOSITIONS BASED THEREON; COMPOSITIONS OF MACROMOLECULAR COMPOUNDS; LAYERED PRODUCTS; LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT ORNON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM; METALLURGY; ORGANIC MACROMOLECULAR COMPOUNDS; PERFORMING OPERATIONS; THEIR PREPARATION OR CHEMICAL WORKING-UP; TRANSPORTING

Die Erfindung betrifft eine Mehrschichtfolie, umfassend zumindest eine obere Schicht a) und eine mittlere Schicht b) aus (Meth)acrylatcopolymeren sowie eine Trägerschicht c) aus Polycarbonat, wobei die obere Schicht a) ein Lichtschutzmittel enthält und aus einem (Meth)acrylatcopolymeren besteht, weiches mit dem Polycarbonat der Trägerschicht c) teilverträgliche Mischungen ausbilden kann, wobei ein aus einer Mischung aus 20 Gew.-% (Meth)acrylatcopolymer und 80 Gew.-% Polycarbonat hergestellter Probekörper eine Bruchdehnung (ISO 527-2) bei 23 C von mindestens 75 % aufweist, die mittlere Schicht b) einen Farbstoff und gegebenenfalls ein Lichtschutzmittel enthält und aus einem identischen oder verschiedenen (Meth)acrylatcopolymeren besteht, welches mit dem Polycarbonat der Trägerschicht c) teilverträgliche Mischungen ausbilden kann, wobei ein aus einer Mischung aus 20 Gew.-% (Meth)acrylatcopolymer und 80 Gew.-% Polycarbonat hergestellter Probekörper eine Bruchdehnung (ISO 527­2-2) bei 23 C von mindestens 75 % aufweist und die Trägerschicht c) aus Polycarbonat besteht, welches gegebenenfalls bis zu 30 Gew.-% des Materials der Schichten a) und b) enthalten kann. Die Erfindung betrifft weiterhin die Herstellung und Verwendungen der Mehrschichtfolie sowie teilverträgliche Polymermischungen aus (Meth)acrylatcopolymeren und Polycarbonat. The invention relates to a multilayered film comprising at least one upper layer a), a middle layer b) made of (meth)acrylate copolymer, and a supporting layer c) made of polycarbonate. Upper layer a) contains a light-stability agent and is made of a (meth)acrylate copolymer that, together with the polycarbonate of supporting layer c), can form partially compatible mixtures. A test piece, which is made from a mixture consisting of 20 % by weight of (meth)acrylate copolymer and 80 % by weight of polycarbonate, has a breaking elongation (ISO 527-2) of at least 75 % at 23 DEG C. The middle layer b) contains a colorant and, optionally, a light-stability agent and is made from an identical or different (meth)acrylate copolymer that, together with the polycarbonate of supporting layer c), can form partially compatible mixtures. A test piece, which is made from a mixture consisting of 20 % by weight of (meth)acrylate copolymer and 80 % by weight of polycarbonate, has a breaking elongation (ISO 527-2) of at least 75 % at 23 DEG C, and the supporting layer c) is made of polycarbonate that, optionally up to 30 % by weight of the material of the layers, can contain a) and b). The invention also relates to the production and uses of the multilayered film and to partially compatible polymer mixtures consisting of (meth)acrylate copolymer and polycarbonate. L'invention concerne un film multicouche comprenant au moins une couche supérieure a) et une couche centrale b) en copolymère (méth)acrylique et une couche de support c), constituée de polycarbonate. La couche supérieure a) contient un agent photoprotecteur et est constituée d'un copolymère (méth)acrylique qui peut former, avec le polycarbonate de la couche de support c), des mélanges partiellement compatibles. Une éprouvette réalisée à partir d'un mélange de 20 % en poids de copolymère (méth)acrylique et de 80 % en poids de polycarbonate présente un allongement à la rupture (ISO 527-2) à 23 DEG C d'au moins 75 %. La couche centrale b) contient un colorant et, éventuellement, un photoprotecteur et elle est constituée du même copolymère (méth)acrylique que celui de la couche supérieure a), ou d'un copolymère (méth)acrylique différent, pouvant former avec le polycarbonate de la couche de support c) des mélanges partiellement compatibles. Une éprouvette réalisée à partir d'un mélange de 20 % en poids de copolymère (méth)acrylique et de 20 % en poids de polycarbonate présente un allongement à la rupture (ISO 527-2-2) à 23 < DEG >C d'au moins 75 %. La couche de support c) est constituée d'un polycarbonate qui, éventuellement, peut contenir jusqu'à 30 % en poids du matériau constituant les couches a) et b). L'invention concerne également la production et les utilisations d'un tel film multicouche, ainsi que des mélanges polymères partiellement compatibles constitués de copolymère (méth)acrylique et de polycarbonate.