Method for producing a hot strip of a bainitic multi-phase steel having a Zn-Mg-Al coating, and a corresponding hot strip

• Main Authors: Mecke, Stefan, Köpper, Nils, Pelz, Christian, Habermann, Maik, Denks, Ingwer, Braun, Michael, Geffert, Ansgar
• Format: Patent
• Language: English
• Published: 29.11.2022
• Subjects: ADVERTISING; ALLOYS; ARRANGEMENTS OR CIRCUITS FOR CONTROL OF INDICATING DEVICESUSING STATIC MEANS TO PRESENT VARIABLE INFORMATION; CALCULATING; CHEMICAL SURFACE TREATMENT; CHEMISTRY; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATIONOR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY IONIMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; COATING MATERIAL WITH METALLIC MATERIAL; COATING METALLIC MATERIAL; COMPUTING; COUNTING; CRYPTOGRAPHY; DIFFUSION TREATMENT OF METALLIC MATERIAL; DISPLAY; EDUCATION; FERROUS OR NON-FERROUS ALLOYS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION INGENERAL; LAYERED PRODUCTS; LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT ORNON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS; METALLURGY; METALLURGY OF IRON; MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; PERFORMING OPERATIONS; PHYSICS; SEALS; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THESURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; TRANSPORTING; TREATMENT OF ALLOYS OR NON-FERROUS METALS

The invention relates to a method for producing a hot-rolled strip composed of a bainitic multi-phase steel and having a Zn-Mg-Al coating, comprising the following steps: melting a steel melt containing (in weight percent): C: 0.04-0.11, Si: <=0.7, Mn: 1.4-2.2, Mo: 0.05-0.5, Al: 0.015-0.1, P: up to 0.02, S: up to 0.01, B: up to 0.006, and at least one element from the group Nb, V, Ti in accordance with the following condition: 0.02<=Nb+V+Ti<=0.20, the remainder being iron including unavoidable steel-accompanying elements resulting from the melting process, casting the steel melt into a preliminary material, in particular a slab or a block or a thin slab, hot rolling the preliminary material into a hot-rolled strip having a final rolling temperature in the range of 800 to 950° C., cooling the hot-rolled strip to a winding temperature less than 650° C., winding the hot-rolled strip at a winding temperature less than 650° C., cooling the wound hot-rolled strip to room temperature in still air, wherein the microstructure of the wound hot-rolled strip then has a bainite fraction greater than 50% after the hot rolling, heating the hot-rolled strip to a temperature greater than 650° C. and less than Ac3, in particular less than Ac1+50° C., cooling the hot-rolled strip to zinc bath temperature, hot-dip coating the heated hot-rolled strip in a zinc alloy molten bath containing (in weight percent): Al: 1.0-2.0, Mg: 1.0-2.0, the remainder being zinc and unavoidable impurities. The invention further relates to the hot-rolled strip produced in accordance with the method above and to shaped, dynamically highly loadable components, in particular motor vehicle parts, that are produced from said hot-roiled strip and that are resistant to corrosive and abrasive influences.