MAGNETIC LUMINESCENT PIGMENT AND A METHOD FOR PRODUCTION THEREOF

• Main Authors: Kazartsev Igor Sergeevich, Torgashova Aleksandra Aleksandrovna, Shchepin Viktor Gennadievich, Voskresenskaya Olga Igorevna, Kornilov Georgij Valentinovich, Kuryatnikov Andrej Borisovich, Manashirov Oshir Yaizgilovich, Vorobev Viktor Andreevich, Sinelnikov Boris Mikhajlovich, Fedorova Elena Mikhajlovna, Ledeneva Ekaterina Andreevna, Pavlov Igor Vasilevich, Pevtsova Larisa Aleksandrovna
• Format: Patent
• Language: English; Russian
• Published: 15.01.2020
• Subjects: ADHESIVES; BOOK COVERS; BOOKBINDING; CHEMICAL PAINT OR INK REMOVERS; CHEMISTRY; COATING COMPOSITIONS, e.g. PAINTS, VARNISHES ORLACQUERS; CORRECTING FLUIDS; DEVICES FOR USE THEREWITH AND NOT OTHERWISE PROVIDEDFOR; DYES; FILES; FILLING PASTES; INKS; LOOSE LEAVES; MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FORELSEWHERE; METALLURGY; MISCELLANEOUS APPLICATIONS OF MATERIALS; MISCELLANEOUS COMPOSITIONS; MOVABLE-STRIP WRITING OR READING APPARATUS; NATURAL RESINS; PAINTS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; PERFORMING OPERATIONS; POLISHES; PRINTED MATTER CHARACTERISED BY IDENTIFICATION OR SECURITYFEATURES; PRINTED MATTER OF SPECIAL FORMAT OR STYLE NOTOTHERWISE PROVIDED FOR; SPECIAL PRINTED MATTER; TRANSPORTING; USE OF MATERIALS THEREFOR; WOODSTAINS

FIELD: chemistry.SUBSTANCE: invention relates to chemical industry and can be used in printing products. Magnetic luminescent pigment based on strontium aluminoferrate, cobalt, each particle of which has both magnetic properties and Stokes fluorescence in the spectral range of 450-750 nm, occurring under the action of exciting radiation lying in the spectral range of wavelengths of 360-1,360 nm. Chemical composition of pigment corresponds to the following empirical formula: (SrCoEuMg)(AlFe)O, where: 0.2≤X≤0.8, 0.0001≤Y≤0.10, 0≤M≤0.3, 0.2≤Z≤0.8. Method of obtaining a magnetic luminescent pigment involves mixing components of a mixture containing oxides of aluminum, iron, cobalt, magnesium, strontium carbonate, aqueous solutions of boric acid and europium chloride. After that, the mixture is homogenized, dried at temperature of 120-240 °C to the state of dusting and calcining at temperature of 1,150-1,350 °C for 4-12 hours.EFFECT: obtaining a pigment, in each particle of which magnetic and luminescent properties are combined, which enables to introduce into circulation new complex machine-readable and visualized protective labels and methods of determining said pigments.6 cl, 1 tbl, 19 ex Изобретение относится к химической промышленности и может быть использовано в полиграфических изделиях. Магнитный люминесцентный пигмент на основе алюмоферрата стронция, кобальта, каждая частица которого обладает как магнитными свойствами, так и стоксовой люминесценцией в спектральном диапазоне 450-750 нм, возникающей под действием возбуждающего излучения, лежащего в спектральном диапазоне длин волн 360-1360 нм. Химический состав пигмента соответствует следующей эмпирической формуле: (SrCoEuMg)(AlFe)O, где: 0,2≤Х≤0,8, 0,0001≤Y≤0,10, 0≤М≤0,3, 0,2≤Z≤0,8. Способ получения магнитного люминесцентного пигмента включает смешение компонентов шихты, содержащей оксиды алюминия, железа, кобальта, магния, карбонат стронция, водные растворы борной кислоты и хлорида европия. После чего шихту гомогенизируют, сушат при температуре 120-240°С до состояния пыления и прокаливают при температуре 1150-1350°С в течение 4-12 часов. Обеспечивается получение пигмента, в каждой частице которого совмещены магнитные и люминесцентные свойства, что позволяет вводить в оборот новые комплексные машиночитаемые и визуализируемые защитные метки и методы их определения. 4 н. и 2 з.п. ф-лы, 1 табл., 19 пр.