METHOD OF SURFACE STRENGTHENING OF DETAILS MADE OF HEAT-RESISTANT NICKEL ALLOY

• Main Authors: OSPENNIKOVA OL'GA GENNADIEVNA, ELISEEV JURIJ SERGEEVICH, TEREKHIN ANDREJ MIKHAJLOVICH, ORLOV MIKHAIL ROMANOVICH, ABRAIMOV NIKOLAJ VASIL'EVICH, SHKRETOV JURIJ PAVLOVICH
• Format: Patent
• Language: English; Russian
• Published: 10.04.2009
• Subjects: CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS ANDNON-FERROUS ALLOYS; CHEMICAL SURFACE TREATMENT; CHEMISTRY; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATIONOR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY IONIMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; COATING MATERIAL WITH METALLIC MATERIAL; COATING METALLIC MATERIAL; DIFFUSION TREATMENT OF METALLIC MATERIAL; FERROUS OR NON-FERROUS ALLOYS; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION INGENERAL; METALLURGY; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLICMATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASSC23 AND AT LEAST ONEPROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25; NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THESURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; TREATMENT OF ALLOYS OR NON-FERROUS METALS

FIELD: metallurgy. ^ SUBSTANCE: invention relates to metallurgy field. Particularly it relates to methods of high-temperature coat strengthening of details made from heat-resistant nickel alloy, and can be used for increasing of strength and durability turbine blades of gas turbine engine. Method includes thermomechanical treatment and recrystallisation annealing of coating. Thermomechanical treatment of coating is implemented by means of hot isostatic pressing in inert gaseous medium at the temperature T, chosen in range T1<T<T2, where T1 - critical brittle temperature, T2 - softening temperature of heat-resistant nickel alloy, and at pressure value 30-150 MPa. Before or after recrystallisation annealing on detail surface can be applied coating layer, containing aluminium, of thickness 5-20 micrometers. ^ EFFECT: increasing of mechanical properties, first of all fatigue resistance of details made of heat-resistant alloy, coating durability increasing. ^ 3 cl, 1 ex Изобретение относится к металлургии, в частности к способам упрочнения жаростойких покрытий деталей из жаропрочных никелевых сплавов, и может быть использовано для увеличения прочности и долговечности лопаток турбин газотурбинных двигателей. Способ включает термомеханическую обработку и рекристаллизационный отжиг покрытия. Термомеханическую обработку покрытия осуществляют путем горячего изостатического прессования в инертной газовой среде при температуре Т, выбираемой в интервале Т1<Т<Т2, где T1 - критическая температура хрупкости покрытия, Т2 - температура разупрочнения жаропрочных никелевых сплавов, и при величине давления 30-150 МПа. До или после рекристаллизационного отжига на поверхность детали может быть нанесен слой покрытия, содержащий алюминий, толщиной 5-20 мкм. Технический результат - повышение механических свойств, прежде всего усталостной прочности деталей из жаропрочных сплавов, а также повышение долговечности покрытия. 2 з.п. ф-лы.