BIODEGRADABLE POLYMERIC COMPOSITION FOR FOOD PACKAGES AND PROCESS FOR PREPARING THE SAME

• Main Authors: BOMBOŞ DANIEL, VELEA SANDA, BLĂJAN OLIMPIU, NEAMŢU CONSTANTIN
• Format: Patent
• Language: English; Romanian
• Published: 30.05.2024
• Subjects: ACCESSORIES, CLOSURES, OR FITTINGS THEREFOR; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F,C08G; CHEMISTRY; COMPOSITIONS BASED THEREON; CONTAINERS FOR STORAGE OR TRANSPORT OF ARTICLES OR MATERIALS,e.g. BAGS, BARRELS, BOTTLES, BOXES, CANS, CARTONS, CRATES,DRUMS, JARS, TANKS, HOPPERS, FORWARDING CONTAINERS; CONVEYING; GENERAL PROCESSES OF COMPOUNDING; HANDLING THIN OR FILAMENTARY MATERIAL; METALLURGY; ORGANIC MACROMOLECULAR COMPOUNDS; PACKAGES; PACKAGING ELEMENTS; PACKING; PERFORMING OPERATIONS; STORING; THEIR PREPARATION OR CHEMICAL WORKING-UP; TRANSPORTING; WORKING-UP

The invention relates to a biodegradable polymer composition to be used for food packages and to a process for preparing the same. According to the invention, the composition consists of the following elements expressed as mass percentage: 60...90% polylactic acid with high molecular mass, 5...25% grape seed oil and/or fatty acid esters from the grape seed oil with fatty alcohols C10-C14, 5...25% biodegradable plasticizer with antioxidant properties, 5...15% freeze-dried and ground grape marc as a filler and antioxidant compound, 2...3% biodegradable surface-active agents and 1...7% essential oils with antimicrobial properties, as such or in admixture, adsorbed on calcinated and finely ground diatomite. The process, as claimed by the invention, has the following stages: a. the polylactic mixture as granules or powder is melted at a temperature ranging between 160...180°C and mixed in the melt with the polyester plasticizer, in a screw mixer, for 5...10 min, at a rotary speed of 50...70 rpm; b. the nanomaterial based on freeze-dried and ground grape marc is added to the mixture while stirring in the same conditions, c. the essential oils previously adsorbed on the calcinated and appropriately ground diatomite are added to the resulting mixture and d. after homogenization, the mixture is hot pressed at a temperature ranging between 170...180°C and a pressure of 140...150 bar and sheeted as foils of suitable dimensions, in order to manufacture packages, using special thermoforming equipments. Invenţia se referă la o compoziţie polimerică biodegradabilă utilizată pentru realizarea ambalajelor alimentare şi la un procedeu de obţinere a acesteia. Compoziţia conform invenţiei este constituită din următoarele elemente exprimate în procente masice: 60...90% acid polilactic cu masa moleculară ridicată, 5...25% ulei de sâmburi de struguri şi/sau esteri ai acizilor graşi din uleiul de sâmburicu alcooli graşi C10 - C14, 5...25% plastifiant biodegradabil cu proprietăţi antioxidante, 5...15% tescovină de struguri, liofilizată şi măcinată, ca filler şi compus cu proprietăţi antioxidante,2...3% agenţi tensioactivi biodegradabili şi 1...7% uleiuri esenţiale cu proprietăţi antimicrobiene luate singure sau în amestec, adsorbite pe diatomită calcinată şi fin măcinată. Procedeul conform invenţiei are următoarele etape de realizare:a) amestecul polilactic granule sau pudră se topeşte la o temperatură cuprinsă între 160...180°C şi se amestecă în topitură cu plastifiantul poliesteric, într-un amestecător cu şnec, timp de 5...10 min. la o viteză de rotaţie cuprinsă între 50...70 rot/min.,b) în amestec se adaugă nanomaterialul bazat pe tescovină liofilizată şi măcinată amestecându-se în aceleaşi condiţii de lucru,c) peste amestecul obţinut se adaugă uleiurile volatile adsorbite în prealabil pe diatomita calcinată şi măcinată la dimensiuni corespunzătoare şid) după omogenizarea amestecului, acesta se presează la cald la o temperatură cuprinsă între 170...180°C cu o presiune de 140...150 bari şi se trage în folii de dimensiuni adecvate în vederea obţinerii ambalajelor cu ajutorul echipamentelor specifice de termoformare.