COMPOSITION AND PROCEDURE FOR RETANNING BOVINE HIDES

• Main Authors: NICULESCU MIHAELA DOINA, CONSTANTIN ANDRA MANUELA, CRUDU MARIAN
• Format: Patent
• Language: English; Romanian
• Published: 30.06.2020
• Subjects: APPARATUS THEREFOR; CHEMICAL TREATMENT OF HIDES, SKINS OR LEATHER, e.g. TANNING,IMPREGNATING, FINISHING; CHEMISTRY; COMPOSITIONS FOR TANNING; HIDES; LEATHER; METALLURGY; PELTS; SKINS

The invention relates to a composition based on protein/collagen and metal/titanium oxides extracted from wastes resulting from mechanical processing of tanned hides and to a process for retanning bovine hides, meant for wet finishing of tanned hides. According to the invention, the composition is prepared starting from 30...35% pretanned leather wastes, 60...70% industrial water and 2...5% lactic acid, the mixture being stirred for 12...24 hours at 60...800 rpm and then compounded with 3...5% zirconium acetate, resulting in a bioproduct as a viscous paste of grey-beige colour containing 60...65% proteinaceous substances, 20...25% Ti-Zr metal oxides, 28...35% ash and 40...45% dry matter, the pH of the 10% solution ranging between 4...4.5. The process, as claimed by the invention, consists in dosing an amount of 3...8% retanning composition in relation with the weight of the tanned, shaved, neutralized and fat-liquored hides, directly in the retanning float, with the following parameters: 100% liquor ratio, temperature of 30°C, pH value of 6.5, and, after 40...60 min, the hide and float appearance is controlled and 0.5% formic acid diluted with water in a ratio of 1:10 is added while stirring, in two portions, for 15...20 min, in order to fix the retanning agent into the fibrillar tissue of hides, the so retanned hide blanks getting a shrinking temperature of 82°C and the phenol concentration in the residual float being of less than 0.7 mg/l, while, after drying and mechanical processing, the crust bovine hides blanks will have physical and mechanical characteristics comparable with nappa leather, namely a stretching resistance in the range 16...21 N/mm, breaking elongation of 95...125%, elongation at 10 N/mm of 50...85% and tearing resistance of 45...55 N/mm. Invenţia se referă la o compoziţie pe bază de proteină/colagen şi oxizi metalici/titan extraşi din deşeuri rezultate la prelucrarea mecanică a pieilor tăbăcite şi la un procedeu pentru retanarea pieilor de bovine destinat finisării umede a pieilor tăbăcite. Compoziţia conform invenţiei se prepară pornind de la 30...35% deşeuri de piele pretăbăcită, 60...70% apă industrială şi 2...5% acid lactic, amestecul fiind agitat timp de 12...24 h la 60...800 rot/min, după care se compoundează cu 3...5% acetat de zirconiu rezultând un bioprodus sub forma unei paste vâscoase de culoare gris-beige, care are în compoziţie substanţe proteice de 60...65%, oxizi metalici Ti-Zr 20...25%, 28...35% cenuşă şi 40...45% substanţă uscată,H-ul soluţiei 10% fiind cuprins între 4...4,5. Procedeul conform invenţiei constă în dozarea unei cantităţi de 3...8% de compoziţie pentru retanare raportată la greutatea pieilor tăbăcite, egalizate, neutralizate şi unse, direct în flota de retanare cu următorii parametri: 100% raport de flotă, temperatura de 30°C, valoareH = 6,5, urmând ca după 40...60 min să se controleze aspectul pieilor şi a flotei adăugându-se apoi sub agitare 0,5% acid formic diluat 1:10 cu apă în două porţii timp de 15...20 min pentru fixarea agentului de retanare în ţesutul fibrilar al pieilor, semifabricatele de piei astfel retanate dobândind o temperatură de contracţie de 82°C, iar concentraţia de fenoli în flota reziduală este de sub 0,7 mg/l, urmând ca, după uscare şi prelucrare mecanică, semifabricatele de piei de bovine crust să aibă caracteristici fizico-mecanice comparabile cu cele ale pieilor de tip nappa, respectiv rezistenţa la tracţiune cuprinsă între 16...21 N/mm, alungirea la rupere de 95...125%, alungirea la 10 N/mm de 50...85% şi rezistenţa la sfâşiere de 45...55 N/mm.