FERRITE AUSTENITE TWO-PHASE STAINLESS STEEL AND MANUFACTURING METHOD THEREOF

• Main Authors: TSUGE SHINJI, KAWA MACHI
• Format: Patent
• Language: English; Japanese
• Published: 11.10.2023
• Subjects: ALLOYS; CHEMISTRY; FERROUS OR NON-FERROUS ALLOYS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUSMETALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHERTREATMENTS; METALLURGY; METALLURGY OF IRON; MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; TREATMENT OF ALLOYS OR NON-FERROUS METALS

To provide a ferrite and austenite two-phase stainless steel plate excellent in hardness and toughness and its manufacturing method.SOLUTION: Steel having a predetermined chemical composition is hot rolled under the conditions that the rolling reduction ratio of rolling at a temperature Tc (°C) or lower is 1.2 or more, is hot-rolled under the condition where the final rolling pass temperature is (Tc-100)°C or higher, by air cooling for 20 seconds or more after the hot rolling, and then cooling at a cooling rate of 1°C/s or more in the temperature range from 800°C to 600°C, a PREN_Mn value is 35.0 or less, and Charpy impact value vE-20°C at -20°C is 100 J/cm2 or more, and a ferrite-austenite two-phase stainless steel plate having a Brinell hardness HBW3000 of 230 or more can be obtained. PREN_Mn value=Cr+3.3(Mo+0.5W)+16N-Mn Tc(°C)=930+50Mo(°C)SELECTED DRAWING: None 【課題】硬度と靭性に優れたフェライト・オーステナイト二相ステンレス鋼板およびその製造方法を提供する。【解決手段】所定の化学組成を有する鋼を、温度Ｔｃ（℃）以下でされる圧延の圧下比が１．２以上であり、圧延最終パス温度を（Ｔｃ－１００）℃以上とする条件で熱間圧延し、前記熱間圧延後に２０秒以上空冷してから８００℃から６００℃の温度区間を冷却速度１℃／ｓ以上で冷却することにより、ＰＲＥＮ＿Ｍｎ値が３５．０以下であり、－２０℃におけるシャルピー衝撃値ｖＥ－２０℃が１００Ｊ／ｃｍ２以上であり、鋼板表層のブリネル硬さＨＢＷ３０００が２３０以上であるフェライト・オーステナイト二相ステンレス鋼板を得ることができる。ＰＲＥＮ＿Ｍｎ値＝Ｃｒ＋３．３（Ｍｏ＋０．５Ｗ）＋１６Ｎ－ＭｎＴｃ（℃）＝９３０＋５０Ｍｏ （℃）【選択図】なし