LAMINATE CONTAINING CELLULOSE NANOFIBER, AND METHOD FOR PRODUCING THE LAMINATE

• Main Authors: NAKATANI TAKESHI, MORITA MASAHIRO, HATAKEYAMA KIYOSHI, HOTTA TAKESHI, YOSHIMATSU TAKEHIRO, HAMAYA TOSHIKI
• Format: Patent
• Language: English; Japanese
• Published: 15.06.2023
• Subjects: APPLYING LIQUIDS OR OTHER FLUENT MATERIALS TO SURFACES, IN GENERAL; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; NANOTECHNOLOGY; PERFORMING OPERATIONS; PROCESSES FOR APPLYING LIQUIDS OR OTHER FLUENT MATERIALS TOSURFACES, IN GENERAL; SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; SPRAYING OR ATOMISING IN GENERAL; TRANSPORTING

To provide a method for producing a laminate having a functional layer that is ideal for use in a variety of industrial applications.SOLUTION: The present invention provides a method for producing a laminate, the method including a step for applying a coating liquid containing an anionically modified cellulose nanofiber onto a support substrate by a pre-metering coating method to form a functional layer, wherein the coating liquid has a viscosity of 50-1000 mPa s at 60 rpm and the functional layer has a thickness of 30 μm or less. Preferably, the anionically modified cellulose nanofiber is an oxidized cellulose nanofiber having a carboxyl group and/or a carboxylate group; or a carboxyalkylated cellulose nanofiber, a phosphorylated cellulose nanofiber, or a sulphated cellulose nanofiber.SELECTED DRAWING: None 【課題】本発明によれば、様々な工業用途に適用させるために最適な機能層を持つ積層体の製造方法を提供することを課題とする。【解決手段】本発明は、支持基材上に、アニオン変性セルロースナノファイバーを含む塗工液を前計量塗工法により塗布して機能層を形成する工程を含み、塗工液の６０ｒｐｍにおける粘度が５０～１０００ｍＰａ・ｓであり、機能層の膜厚３０μｍ以下である、積層体の製造方法を提供する。前記アニオン性セルロースナノファイバーは、カルボキシル基及び／またはカルボキシレート基を有する酸化セルロースナノファイバーであること、カルボキシアルキル化セルロースナノファイバー、リン酸エステル化セルロースナノファイバー、又は硫酸エステル化セルロースナノファイバーであることが好ましい。【選択図】なし