METHOD FOR MELTING HIGH MANGANESE-CHROMIUM-CONTAINING STEEL

• Main Author: YOSHIDA ATSUHIKO
• Format: Patent
• Language: English; Japanese
• Published: 08.12.2014
• Subjects: CHEMISTRY; METALLURGY; METALLURGY OF IRON; PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OFWROUGHT-IRON OR STEEL; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS

PROBLEM TO BE SOLVED: To provide a method for melting high manganese-chromium-containing steel, by which variation in Mn and Cr can be suppressed, and also productivity can be improved.SOLUTION: The method for melting high manganese-chromium-containing steel comprises: a first step of adding an alloy containing Mn and Cr to molten iron in a converter and carrying out decarbonization refining of the molten iron; a second step of, when tapping molten steel subjected to the decarbonization refining into a ladle, adding a ferroalloy to the molten steel; and a third step of adding the ferroalloy to molten iron after the second step in secondary refining equipment and carrying out secondary refining. When a total ferroalloy added through the first to the third steps is set as 100%, 30 to 45% of the total ferroalloy is added in the first step; 30 to 45% of the total ferroalloy is added in the second step; and 10 to 40% of the total ferroalloy is added in the third step. 【課題】高マンガンクロム含有鋼を溶製するに際して、ＭｎやＣｒのバラツキを抑制することができて、且つ生産性も向上させることができるようにする。【解決手段】本発明では、転炉においてＭｎ及びＣｒを含有する合金鉄を添加すると共に溶銑の脱炭精錬を行う第１工程と、脱炭精錬後の溶鋼を転炉から取鍋へ出鋼する際に前記合金鉄を添加する第２工程と、二次精錬設備において第２工程後の溶銑に前記合金鉄を添加すると共に二次精錬を行う第３工程とを有しており、前記第１工程から第３工程に亘って添加する全体の合金鉄を１００％としたとき、前記第１工程においては前記全体の合金鉄に対して３０〜４５％の合金鉄を添加し、前記第２工程においては前記全体の合金鉄に対して３０〜４５％の合金鉄を添加し、前記第３工程においては全体の合金鉄に対して１０〜４０％の合金鉄を添加する。【選択図】図１