Extrusion Coating Polyethylene Composition
Extrusion coating polyethylene compositions A), comprising B) a polymer blend comprising a) 5 wt% - 60 wt% of a long chain branched, low-density polyethylene, having - a melt index MFR 2 of 2.5 to 10.0 g/10 min, according to ISO 1133, - a density of 910 to 935 kg/m 3 , according to ISO 1183-1987, an...
Saved in:
Main Authors | , , |
---|---|
Format | Patent |
Language | English French German |
Published |
20.10.2010
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Extrusion coating polyethylene compositions A), comprising
B) a polymer blend comprising
a) 5 wt% - 60 wt% of a long chain branched, low-density polyethylene, having
- a melt index MFR 2 of 2.5 to 10.0 g/10 min, according to ISO 1133,
- a density of 910 to 935 kg/m 3 , according to ISO 1183-1987,
and
- a dynamic viscosity · 0.05 (190°C) at a shear rate of 0.05 rad/s and a dynamic viscosity · 300 rad/s (190°C) which satisfy the following relationship: · 300 ¤ 108 Pa * s + 0.0253 * · 0.05
and/or
- a phase shift ´ 0.5 (190°C) at a frequency of 0.5 rad/s and a phase shift ´ 300 (190°C) at a frequency of 300 rad/s, which satisfy the following relationship: tan ´ 300 ¥ 0.45 + 0.164 * tan ´ 0.05
and
b) 95 wt% - 40 wt% of a bimodal metallocene-based linear low density polyethylene terpolymer having a melt index MFR 2 of from 3 to 40 g/10 min, according to ISO 1133, and a density of from 900 to 935 kg/m 3 , according to ISO 1183-1987, which has been produced by polymerising ethylene and two alpha-olefin comonomers having from 4 to 10 carbon atoms in at least two polymerisation stages in the presence of a metallocene catalyst. and
C) 1wt% - 50wt% based on the total weight of the polymer blend B) of a non-thermoplastic filler and
extrusion coating polyethylene compositions D, comprising 40 - 60 wt% of the polyethylene composition A), and 60 - 40 wt% of polymer blend B and their use. |
---|---|