Method for producing copolymerized polyamide
The present invention relates to a method for producing a copolymerized polyamide, which is capable of efficiently obtaining a copolymerized polyamide having good quality, and which comprises the following first step and second step. A first step: a step for preparing a mixed solution by adding soli...
Saved in:
Main Authors | , , , , , , , , |
---|---|
Format | Patent |
Language | Chinese English |
Published |
15.04.2022
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | The present invention relates to a method for producing a copolymerized polyamide, which is capable of efficiently obtaining a copolymerized polyamide having good quality, and which comprises the following first step and second step. A first step: a step for preparing a mixed solution by adding solid adipic acid (B) to liquid epsilon-caprolactam (A) and mixing epsilon-caprolactam (A) and adipic acid (B) at a temperature of 69 DEG C or more and less than 115 DEG C to prepare a mixed solution in which the amount of epsilon-caprolactam (A) used is 1-20 moles per 1 mole of adipic acid (B); and a second step for obtaining a copolymerized polyamide by mixing the mixed solution obtained in the first step with hexamethylenediamine (C) and then reacting the mixture with the hexamethylenediamine (C).
本发明涉及共聚聚酰胺的制造方法,其能够有效地获得品质良好的共聚聚酰胺,且包括下述的第一工序和第二工序。第一工序:将ε-己内酰胺(A)与己二酸(B)以69℃以上且低于115℃进行混合,从而制备混合液的工序,其中,向液态的ε-己内酰胺(A)中添加固态的己二酸(B),进行ε-己内酰胺(A)与己二酸(B)的混合,制备ε-己内酰胺(A)的用量相对于己二酸(B)1摩尔为1~20摩尔的混合液;第二工序:将通过第一工序而得到的混合液与六亚甲基二胺(C)混合 |
---|---|
Bibliography: | Application Number: CN202080063808 |