Effects of High Magnetic Field on Microstructure and Properties of Low Aspect Ratio Bi2Sr2CaCu2Ox/AgMg Wire
Here,we report the effect of an 8 T magnetic field on the microstructure and properties of a reetangular Bi2Sr2CaCu20x/AgMg(Bi2212/AgMg)conductor with low aspect ratio.The magnetic field was applied during split melt process with the field direction perpendicular and parallel to the wide surface of...
Saved in:
Published in | 钢铁研究学报:英文版 no. S2; pp. 1048 - 1053 |
---|---|
Main Author | |
Format | Journal Article |
Language | English |
Published |
2012
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | Here,we report the effect of an 8 T magnetic field on the microstructure and properties of a reetangular Bi2Sr2CaCu20x/AgMg(Bi2212/AgMg)conductor with low aspect ratio.The magnetic field was applied during split melt process with the field direction perpendicular and parallel to the wide surface of the conductors.After heat treatment,the conductors were electrically characterized using four-point critical current measurements as a function of magnetic field and magnetic field orientation relative to the conductor.The superconducting transition and magnetization hysteresis were measured using a SQUID magnetometer.The microstructure was characterized using scanning electron microscopy.It was found that the presence of magnetic field during split melt processing enhances the electrical transport and magnetic behavior.The magnetic field increases the Bi2212 grains alignment and long range texture within filaments and bridges between filaments by textured growth of Bi2212 phase. |
---|---|
Bibliography: | 11-3678/TF LIU Xiao-tao;SCHWARTZ Justin;CUI Jian-zhong;The Key Lab of Electromagnetic Processing of Materials of Ministry Education,Notheastern University;Department of Materials Science of Engineering,North Carolina State University |
ISSN: | 1006-706X 2210-3988 |