Microwave absorption properties of SiC@SiO2@Fe3O4 hybrids in the 2–18 GHz range

To enhance the microwave absorption performance of silicon carbide nanowires（SiCNWs）, SiO_2 nanoshells with a thickness of approximately 2 nm and Fe_3O_4 nanoparticles were grown on the surface of SiCNWs to form SiC@SiO_2@Fe_3O_4 hybrids. The microwave absorption performance of the SiC@SiO_2@Fe_3O_4...

Full description

Saved in:
Bibliographic Details
Published in矿物冶金与材料学报：英文版 Vol. 24; no. 7; pp. 804 - 813
Main Author Peng Zhou Jun-hong Chen Meng Liu Peng Jiang Bin Li Xin-mei Hou
Format Journal Article
LanguageEnglish
Published 2017
Subjects
SiC
千兆赫
微波吸收性能
杂化材料
杂种表现
硅纳米线
纳米粒子
频率范围
Online AccessGet full text

Cover

More Information
Summary:To enhance the microwave absorption performance of silicon carbide nanowires（SiCNWs）, SiO_2 nanoshells with a thickness of approximately 2 nm and Fe_3O_4 nanoparticles were grown on the surface of SiCNWs to form SiC@SiO_2@Fe_3O_4 hybrids. The microwave absorption performance of the SiC@SiO_2@Fe_3O_4 hybrids with different thicknesses was investigated in the frequency range from 2 to 18 GHz using a free-space antenna-based system. The results indicate that SiC@SiO_2@Fe_3O_4 hybrids exhibit improved microwave absorption. In particular, in the case of an SiC@SiO_2 to iron（III） acetylacetonate mass ratio of 1：3, the microwave absorption with an absorber of 2-mm thickness exhibited a minimum reflection loss of-39.58 d B at 12.24 GHz. With respect to the enhanced microwave absorption mechanism, the Fe_3O_4 nanoparticles coated on SiC@SiO_2 nanowires are proposed to balance the permeability and permittivity of the materials, contributing to the microwave attenuation.
Bibliography:11-5787/TF
silicon carbide nanowires hybrids microwave absorption mechanism impedance match
To enhance the microwave absorption performance of silicon carbide nanowires（SiCNWs）, SiO_2 nanoshells with a thickness of approximately 2 nm and Fe_3O_4 nanoparticles were grown on the surface of SiCNWs to form SiC@SiO_2@Fe_3O_4 hybrids. The microwave absorption performance of the SiC@SiO_2@Fe_3O_4 hybrids with different thicknesses was investigated in the frequency range from 2 to 18 GHz using a free-space antenna-based system. The results indicate that SiC@SiO_2@Fe_3O_4 hybrids exhibit improved microwave absorption. In particular, in the case of an SiC@SiO_2 to iron（III） acetylacetonate mass ratio of 1：3, the microwave absorption with an absorber of 2-mm thickness exhibited a minimum reflection loss of-39.58 d B at 12.24 GHz. With respect to the enhanced microwave absorption mechanism, the Fe_3O_4 nanoparticles coated on SiC@SiO_2 nanowires are proposed to balance the permeability and permittivity of the materials, contributing to the microwave attenuation.