Effect of Nb and alloying elements on interface reaction between high Nb-containing TiAl alloys and ZrO_2-based ceramic moulds

• Published in: 中国铸造：英文版 no. 5; pp. 362 - 366
• Main Author: Liang Yang Wen-bin Kan You-wei Zhang Chun-ling Bao Shi-bing Liu Jun-pin Lin
• Format: Journal Article
• Language: English
• Published: 2015
• ISSN: 1672-6421; 2365-9459

In the present study, Ti-45Al-（6, 7, 8）Nb（at%） and Ti-45Al-8Nb-0.5（Mn, Si, Y, B） alloys were prepared by arc melting and casting into Zr O2（Y2O3 stabilized） ceramic moulds to study the effect of alloying elements Nb and Mn, Si, Y, B on the interfacial reaction between casting Ti Al alloys and ceramic moulds by SEM, and the elements＇ distribution in the interface reaction layer by line scanning. The results showed that with an increase in Nb content, the interfacial reaction weakened and the thickness of the reaction layer decreased gradually. The interface reaction thickness of the alloys with Nb content of 6, 7, 8at% were 60, 34 and 26 μm, respectively. Clearly, the addition of 8at% Nb to Ti-45 Al is the best for the thickness of the reaction layer. The addition of Nb would form a Nb-rich film in the reaction layer, which could reduce the solubility of oxygen in the interface, and suppress further diffusion of oxygen to the matrix. If the same content of Mn, Si, Y, or B alloying elements were added respectively to Ti-45Al-8Nb, the thickness of the interface reaction layer from large to small was as follows： Mn〉Si〉Y〉B. The interface reaction thickness increased after 0.5at% Mn added, had no obvious change after 0.5at% Si addition, and decreased after adding 0.5at% Y or B. The introduced elements, which formed a protective film or/and promoted the formation of a dense aluminum oxide layer, would be of benefit to the resistance of interfacial reaction.