Cyelie Oxidation Resistance of In718 Superalloy Treated by Laser Peening

• Published in: 武汉理工大学学报：材料科学英文版 no. 4; pp. 808 - 812
• Main Author: BAI Yuehuan HUA Yinqun RONG Zhen YE Yunxia XUE Qing LIU Haixia CHEN Ruifang
• Format: Journal Article
• Language: English
• Published: 2015
• Subjects: GH4169高温合金; IN718合金; 扫描电子显微镜; 抗氧化; 抗高温氧化性能; 激光冲击处理; 表面形貌; 透射电子显微镜
• ISSN: 1000-2413; 1993-0437

The aim of this study was to improve the cyclic oxidation resistance of In718 superalloy by laser peening（LP）. Specimens were treated by LP from one to three times, respectively. The cyclic oxidation tests at 900 ℃ for periods up to 2 h were conducted. Changes of the top surface morphology and microstructure were analyzed by scanning electron microscope （SEM）, energy-dispersive spectra （EDS）, transmission electron microscope （TEM） and X-ray diffraction technique （XRD）, respectively. The weights were measured between the oxidation cycles to assess the oxidation of the specimens. The top surface microstructure after LP was characterized by highly tangled and dense dislocation arrangements and a high amount of twins. Protective oxidation layer was generated more quickly on the surface treated by LP. The average oxidation rate was about 50 % lower. A tiny homogeneous oxidation layer containing （Fe,Cr）2O3, NiCrO3 and Ni（A1,Cr）2O4 spinel was generated on the surface. The experimental results of cyclic oxidation tests show that specimens treated by LP have a better high temperature oxidation resistance, and the antistrip performance of the oxidation layer improves. Moreover, the effects of LP are strengthened with the increase of laser peening.