Comparison of thermoluminescence spectra of MgB407 doped with dysprosium and manganese
A series of magnesium borate phosphors MgB4O7：Dy, MgB4O7：Mn and MgB4O7：Dy,Mn were prepared and their ther-moluminescence （TL） emission spectra were measured. TL emission bands in 480, 575 and 660 nm at 200 and 360 oC were observed in the MgB4O7：Dy due to the transitions of the trivalent rare earth i...
Saved in:
| Published in | 中国稀土学报：英文版 Vol. 31; no. 11; pp. 1039 - 1042 |
|---|---|
| Main Author | |
| Format | Journal Article |
| Language | English |
| Published |
2013
|
| Subjects | |
| Online Access | Get full text |
Cover
Loading…
| Summary: | A series of magnesium borate phosphors MgB4O7：Dy, MgB4O7：Mn and MgB4O7：Dy,Mn were prepared and their ther-moluminescence （TL） emission spectra were measured. TL emission bands in 480, 575 and 660 nm at 200 and 360 oC were observed in the MgB4O7：Dy due to the transitions of the trivalent rare earth ions Dy3＋. The glow peaks of broad wavelength band around~580 nm at 180 and~290 oC were observed in MgB4O7：Mn due to the emission of Mn2＋ions. The main glow peak of MgB4O7 co-doped with Dy and Mn appeared in 580 nm at~360 oC. When MgB4O7 was co-doped with Dy （0.5 mol.%） and different concentrations of Mn （0.01 mol.%-1.0 mol.%）, the peak in 580 nm at 360 °C was intensified and broadened as the concentration of Mn increased, while the peaks in 480, 680 and 750 nm below 300 °C remained the characteristic emission of Dy3＋and were reduced in intensity. The emission spectra of the MgB4O7：Dy,Mn phosphor showed that the competitive de-excitation processes between Dy3＋and Mn2＋existed and the energy transfer occurred from Dy3＋to Mn2＋. These results meant that rare earth and Mn ions in MgB4O7：Dy,Mn might cause the formation of defects complex that dominated the traps and recombination. |
|---|---|
| Bibliography: | 11-2788/TF TAN Zhijian LAN Tingting GAO Li ZHANG Chunxiang LIU Xiaowei LUO Daling TANG Qiang （1. School of Physics Science and Engineering, Sun Yat-sen University, Guangzhou 510275, China; 2. School of Sciences, South China University of Technology, Guangzhou 510640, China） magnesium borate; therrnoluminescence; dysprosium; manganese; rare earths A series of magnesium borate phosphors MgB4O7：Dy, MgB4O7：Mn and MgB4O7：Dy,Mn were prepared and their ther-moluminescence （TL） emission spectra were measured. TL emission bands in 480, 575 and 660 nm at 200 and 360 oC were observed in the MgB4O7：Dy due to the transitions of the trivalent rare earth ions Dy3＋. The glow peaks of broad wavelength band around~580 nm at 180 and~290 oC were observed in MgB4O7：Mn due to the emission of Mn2＋ions. The main glow peak of MgB4O7 co-doped with Dy and Mn appeared in 580 nm at~360 oC. When MgB4O7 was co-doped with Dy （0.5 mol.%） and different concentrations of Mn （0.01 mol.%-1.0 mol.%）, the peak in 580 nm at 360 °C was intensified and broadened as the concentration of Mn increased, while the peaks in 480, 680 and 750 nm below 300 °C remained the characteristic emission of Dy3＋and were reduced in intensity. The emission spectra of the MgB4O7：Dy,Mn phosphor showed that the competitive de-excitation processes between Dy3＋and Mn2＋existed and the energy transfer occurred from Dy3＋to Mn2＋. These results meant that rare earth and Mn ions in MgB4O7：Dy,Mn might cause the formation of defects complex that dominated the traps and recombination. |
| ISSN: | 1002-0721 2509-4963 |