镍钛合金的溶胶-凝胶法多孔TiO2薄膜表面改性(英文)
Saved in:
Published in | 中国有色金属学报:英文版 Vol. 22; no. 7; pp. 1661 - 1666 |
---|---|
Main Author | |
Format | Journal Article |
Language | English |
Published |
2012
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Bibliography: | FU Tao1,2,WU Xiao-ming1,WU Feng3,L UO Meng1,DONG Bing-hui1,JI Yuan1 1.Key Laboratory of Biomedical Information Engineering of Ministry of Education,School of Life Science and Technology,Xi’an Jiaotong University,Xi’an 710049,China;2.State Key Laboratory of Metastable Materials Science and Technology,Yanshan University,Qinhuangdao 066004,China;3.College of Medicine,Xi’an Jiaotong University,Xi’an 710061,China 43-1239/TG NiTi alloy;titania;sol?gel method;hydrophilicity;corrosion resistance Titania films with nano-sized pores were prepared on the NaOH?HCl pretreated NiTi alloy substrate by sol?gel method.A crack-free film is obtained for the sample with a dense inner layer and a porous outside layer(sample TC1+1).The X-ray diffraction shows that the titania films are composed of anatase,and a little Ni4Ti3 phase in the heat treated substrate is also detected.The X-ray photoelectron spectroscopy results indicate that the titania film completely covered the NiTi substrate for sample TC1+1.The sample TC1+1 is hydrophilic with a contact angle about 20°,and UV illumination treatment for 15 min further decreases the contact angle to(9.2±3.2)°.The potentiodynamic polarization test in 0.9% NaCl solution reveals a better corrosion resistance of sample TC1+1 than the polished NiTi sample. |
---|---|
ISSN: | 1003-6326 |