稀土盐浸泡镁合金微弧氧化膜层的制备及性能（英文）

Saved in:
Bibliographic Details
Published in中国有色金属学报：英文版 Vol. 22; no. 7; pp. 1647 - 1654
Main Author 刘峰 李玉洁 顾佳婧 严青松 罗强 蔡启舟
Format Journal Article
LanguageEnglish
Published 2012
Subjects
AZ91D镁合金微弧氧化Y2O3-ZrO2-MgO复合膜腐蚀性能耐热性
Online AccessGet full text

Cover

More Information
Bibliography:AZ91D magnesium alloy;micro-arc oxidation（MAO）;Y2O3-ZrO2-MgO composite coating;corrosion behavior;thermal stability
43-1239/TG
A composite ceramic coating containing Y2O3-ZrO2-MgO（YSZ-MgO） was prepared on AZ91D magnesium alloy,which was immersed in Y（NO3）3 aqueous solution as pretreatment,by micro-arc oxidation（MAO） process.The morphology,elemental and phase compositions,corrosion behavior and thermal stability of the coatings were studied by SEM,EDX,XRD,electrochemical corrosion test,high temperature oxidation and thermal shock test.The results show that the coating mainly consists of ZrO2,Y2O3,MgO,Mg2SiO4,and MgF2.Among these compounds,Y2O3 accounts for 26.7% of（Y2O3 ＋ ZrO2）.The thickness of YSZ-MgO coating is smaller than that of ZrO2-MgO coating,but its compactness and surface roughness are better than those of ZrO2-MgO coating.YSZ-MgO coating has a good corrosion resistance,and its corrosion rate in 5% NaCl aqueous solution is lower than that of ZrO2-MgO and only about 8.5% of that of AZ91D magnesium alloy.After oxidation at 410 °C,the mass gain of AZ91D magnesium alloy presents a linear increase with the oxidation time.The YSZ-MgO coating and ZrO2-MgO coating can remarkably decrease the oxidation mass gain.The oxidation mass gain of YSZ-MgO coating is lower than that of ZrO2-MgO coating,especially during a long oxidation period.The thermal shock resistance of YSZ-MgO coating is superior to ZrO2-MgO coating.
LIU Feng1,2,LI Yu-jie1,GU Jia-jing1,YAN Qing-song2,LUO Qiang1,CAI Qi-zhou1 1.State Key Laboratory of Material Processing and Die and Mould Technology,Huazhong University of Science and Technology,Wuhan 430074,China;2.National Defense Key Disciplines Laboratory of Light Alloy Processing Science and Technology,Nanchang Hangkong University,Nanchang 330063,China
ISSN:1003-6326