金属热还原法制备V-Ti-Fe中间合金(英文)
Saved in:
Published in | 中国有色金属学报:英文版 Vol. 22; no. 6; pp. 1507 - 1512 |
---|---|
Main Author | |
Format | Journal Article |
Language | English |
Published |
2012
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Bibliography: | 43-1239/TG V-Ti-Fe master alloys were prepared by metaUothermic reduction method, and the influences of the mass ratio of V205 to TiO2, Al and Al-Mg alloy addition amounts on the metal recovery rates and alloy compositions were investigated. The results show that appropriate technological parameters are: the mass ratio of V205 to TiO2 is 0.5:1, Al addition represents 95% of the theoretical value, and the Al-Mg alloy addition amount is one third that of the Al addition. The results from energy spectrum analysis show that V and Fe distribute uniformly in the prepared alloy, while the segregation for Ti, i.e. Ti-rich phase is detected. A spray refming process was carried out to reduce the impurity contents of Al and O in the prepared alloys. The Al content drops from 4.27% to 1.86%, and the O content drops from 2.10% to 0.91% after the refining process. WANG Bin1, LIU Kui-ren1, CHEN Jian-she, GAO Teng-yue, HE Ji-lin2 1. School of Materials and Metallurgy, Northeastern University, Shenyang 110819, China; 2. Ningxia Orient Nonferrous Metals Group Co. Ltd., Shizuishan 753000, China V-Ti-Fe master alloys; metallothermic reduction method; recovery rates; refining process |
---|---|
ISSN: | 1003-6326 |