Influence of Negative Bias Voltage on the Mechanical and Tribological Properties of MoS_2/Zr Composite Films

MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage on the composite film properties,including adhesion strength,micro-hardness,thickness a...

Full description

Saved in:
Bibliographic Details
Published in武汉理工大学学报：材料科学英文版 Vol. 26; no. 3; pp. 412 - 416
Main Author SONG Wenlong DENG Jianxin YAN Pei WU Ze ZHANG Hui ZHAO Jun AI Xing
Format Journal Article
LanguageEnglish
Published 2011
Subjects
复合膜
多弧离子镀
摩擦学性能
显微硬度
机械
滑动速度
硬质合金
负偏压
Online AccessGet full text

Cover

More Information
Summary:MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage on the composite film properties,including adhesion strength,micro-hardness,thickness and tribological properties were investigated.The results showed that proper negative bias voltage could significantly improve the mechanical and tribological properties of composite films.The effects of negative bias voltage on film properties were also put forward.The optimal negative bias voltage was -200 V under this experiment conditions.The obtained composite films were dense,the adhesion strength was about 60 N,the thickness was about 2.4 μm,and the micro-hardness was about 9.0 GPa.The friction coefficient and wear rate was 0.12 and 2.1×10-7 cm3/N·m respectively after 60 m sliding operation against hardened steel under a load of 20 N and a sliding speed of 200 rev·min-1.
Bibliography:42-1680/TB
medium-frequency magnetron sputtering multi-arc ion plating negative bias voltage MoS2/Zr composite films tribological properties
MoS2/Zr composite films were deposited on the cemented carbide YT14 （WC＋14%TiC＋6%Co） by medium-frequency magnetron sputtered and coupled with multi-arc ion plated techniques.The influence of negative bias voltage on the composite film properties,including adhesion strength,micro-hardness,thickness and tribological properties were investigated.The results showed that proper negative bias voltage could significantly improve the mechanical and tribological properties of composite films.The effects of negative bias voltage on film properties were also put forward.The optimal negative bias voltage was -200 V under this experiment conditions.The obtained composite films were dense,the adhesion strength was about 60 N,the thickness was about 2.4 μm,and the micro-hardness was about 9.0 GPa.The friction coefficient and wear rate was 0.12 and 2.1×10-7 cm3/N·m respectively after 60 m sliding operation against hardened steel under a load of 20 N and a sliding speed of 200 rev·min-1.
ISSN:1000-2413
1993-0437