Destruction of charge ordering phase in La_（0.4）Ca_（0.6）MnO_3 induced by low Cr doping

Polycrystalline samples of La0.4Cao.6Mn1-xCrxO3 （x = 0.00, 0.02, 0.04, 0.06） were prepared by the solid state reaction method. The influence of Cr3＋ substitution for Mn3＋ on the magnetic property and charge ordering phase of La0.4Ca0.6MnO3 was studied through the measurements of X-ray diffraction （X...

Full description

Saved in:
Bibliographic Details
Published in稀有金属：英文版 Vol. 30; no. 3; pp. 241 - 246
Main Author PENG Zhensheng YANG Gang WANG Guiying TANG Yonggang GUO Huanyin MAO Qiang
Format Journal Article
LanguageEnglish
Published 2011
Subjects
Cr掺杂
反铁磁性
固态反应法
电子自旋共振
电荷有序
诱导
销毁
验证实验
Online AccessGet full text

Cover

More Information
Summary:Polycrystalline samples of La0.4Cao.6Mn1-xCrxO3 （x = 0.00, 0.02, 0.04, 0.06） were prepared by the solid state reaction method. The influence of Cr3＋ substitution for Mn3＋ on the magnetic property and charge ordering phase of La0.4Ca0.6MnO3 was studied through the measurements of X-ray diffraction （XRD）, magnetization-temperature （M-T） curves and electron spin resonance （ESR） spectra. The experimental results indicate that the mother＇s body of La0.4Ca0.6MnO3 has very complicated magnetic structure, exhibits charge ordering phase at 258 K, and shows long-range strongly correlated charge ordering-antiferromagnetism （CO-AFM） phase from 175 to 50 K. Spin glass state appears when the temperature decreases to about 41 K. When the Cr substitution amount is x = 0.06, the charge ordering phase of the mother＇s body is de-stroyed, because the Cr3＋ substitution for Mn3＋ destroys the spin order of CE-type antiferromagnetism, and thus leads to the melting of charge ordering. It is verified experimentally that the strong coupling between charge order and spin order exists in the charge order system of CE-type antiferromagnetism.
Bibliography:perovskite manganite; chromium; doping; charge ordering; spin-glass state
Polycrystalline samples of La0.4Cao.6Mn1-xCrxO3 （x = 0.00, 0.02, 0.04, 0.06） were prepared by the solid state reaction method. The influence of Cr3＋ substitution for Mn3＋ on the magnetic property and charge ordering phase of La0.4Ca0.6MnO3 was studied through the measurements of X-ray diffraction （XRD）, magnetization-temperature （M-T） curves and electron spin resonance （ESR） spectra. The experimental results indicate that the mother＇s body of La0.4Ca0.6MnO3 has very complicated magnetic structure, exhibits charge ordering phase at 258 K, and shows long-range strongly correlated charge ordering-antiferromagnetism （CO-AFM） phase from 175 to 50 K. Spin glass state appears when the temperature decreases to about 41 K. When the Cr substitution amount is x = 0.06, the charge ordering phase of the mother＇s body is de-stroyed, because the Cr3＋ substitution for Mn3＋ destroys the spin order of CE-type antiferromagnetism, and thus leads to the melting of charge ordering. It is verified experimentally that the strong coupling between charge order and spin order exists in the charge order system of CE-type antiferromagnetism.
11-2112/TF
ISSN:1001-0521
1867-7185