Effect of SeO2 on corrosion resistance of micro-arc oxidation

In order to make titanium alloy implants have better corrosion resistance in the human body, selenium-containing coating was added to the surface of Ti6Al7Nb through micro-arc oxidation. The results indicate that the coating has a higher thickness and lower roughness after the addition of selenium e...

Full description

Saved in:
Bibliographic Details
Published inSurface engineering Vol. 39; no. 7-12; pp. 797 - 806
Main Authors Zhang, D.F., Zheng, R., Chen, X.W., Zhang, G.H.
Format Journal Article
LanguageEnglish
Published London, England SAGE Publications 02.12.2023
Subjects
SeO2
coatings
roughness
thickness
titanium alloy
SBF solution
corrosion resistance
Micro-arc oxidation
Online AccessGet full text

Cover

More Information
Summary:In order to make titanium alloy implants have better corrosion resistance in the human body, selenium-containing coating was added to the surface of Ti6Al7Nb through micro-arc oxidation. The results indicate that the coating has a higher thickness and lower roughness after the addition of selenium element. XRD, SEM, and XPS analysis showed that selenium element was successfully added into the coating. Then the dynamic polarization curve and EIS indicate that the prepared samples have better corrosion resistance in SBF solution compared to the unadded samples, (i corr ) and (E corr ) are 2.695 × 10−8 A·cm−2 and 0.101 V, respectively. The addition of selenium helps to improve the biological corrosion resistance of the sample in body fluids.
ISSN:0267-0844
1743-2944
DOI:10.1080/02670844.2023.2259529