The decomposition of the beta' phase in Cu-25.7Zn-3.1Al and Cu-17.9Zn-5.4Al shape-memory alloys was studied. The B2- > DO3 order transition was not completely suppressed by quenching in icy water. The aging process at temperatures below 400 deg C involved the formation of bainite or a phase....
Saved in:
Published in | Materiali in tehnologije Vol. 40; no. 4; pp. 153 - 156 |
---|---|
Main Authors | , , |
Format | Journal Article |
Language | Slovenian |
Published |
01.07.2006
|
Online Access | Get full text |
Cover
Loading…
Summary: | The decomposition of the beta' phase in Cu-25.7Zn-3.1Al and Cu-17.9Zn-5.4Al shape-memory alloys was studied. The B2- > DO3 order transition was not completely suppressed by quenching in icy water. The aging process at temperatures below 400 deg C involved the formation of bainite or a phase. In specimens aged at higher temperatures the alpha phase was observed. The activation energies of a precipitation in the Cu-25.7Zn-3.1Al alloy and Cu-17.9Zn-5.4Al alloy were determined to be 109.85 kJ mol-1 and 132.12 kJ mol-1, respectively. The formation of gamma precipitates was not observed. |
---|---|
Bibliography: | ObjectType-Article-2 SourceType-Scholarly Journals-1 ObjectType-Feature-1 content type line 23 |
ISSN: | 1580-2949 1580-3414 |