HIGH NITROGEN AUSTENITIC STAINLESS STEEL PRECIPITATION DURING ISOTHERMAL ANNEALING
The time-temperature-precipitation in high-nitrogen austenitic stainless steel was investigated using light optical microscopy, transmission electron microscopy, selected area diffraction and energy-dispersive X-ray spectroscopy. The isothermal precipitation kinetics curves and the corresponding pre...
Saved in:
Published in | Materiálové inžinierstvo Vol. 23; no. 2; p. 84 |
---|---|
Main Authors | , , , |
Format | Journal Article |
Language | English |
Published |
Zilina
University of Zilina, Faculty of Mechanical Engineering
01.04.2016
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | The time-temperature-precipitation in high-nitrogen austenitic stainless steel was investigated using light optical microscopy, transmission electron microscopy, selected area diffraction and energy-dispersive X-ray spectroscopy. The isothermal precipitation kinetics curves and the corresponding precipitation activation energy were obtained. The diffusion activation energy of M2N precipitation is 129 kJ.mol-1. The results show that critical temperature for M2N precipitation is about 825°C with the corresponding incubation period 2.5 min. |
---|---|
Bibliography: | ObjectType-Article-1 SourceType-Scholarly Journals-1 ObjectType-Feature-2 content type line 23 |
ISSN: | 1335-0803 1338-6174 |