Luminescence and stability of Tb doped CaF2 nanoparticles

• Published in: RSC advances Vol. 13; no. 8; pp. 5353 - 5366
• Main Authors: Hasabeldaim, E H H, Swart, H C, Kroon, R E
• Format: Journal Article
• Language: English
• Published: Cambridge Royal Society of Chemistry 06.02.2023; The Royal Society of Chemistry
• Subjects: Calcium fluoride; Chemistry; Cross relaxation; Defects; Energy transfer; Luminescence; Nanoparticles; Optical properties; Photoelectrons; Photoluminescence; Temperature dependence; Thermoluminescence; Ultraviolet radiation
• ISSN: 2046-2069
• DOI: 10.1039/d2ra07897j

Luminescence properties of CaF2:Tb3+ nanoparticles were studied in order to investigate the effect of CaF2 native defects on the photoluminescence dynamics of Tb3+ ions. Incorporation of Tb ions into the CaF2 host was confirmed by X-ray diffraction and X-ray photoelectron spectroscopy. Cross-relaxation energy transfer was observed from the photoluminescence spectra and decay curves upon excitation at 257 nm. However, the unusual long lifetime of the Tb3+ ion as well as the decreasing trend of emission lifetime of the 5D3 level suggested the involvement of traps, which were further investigated by using temperature-dependent photoluminescence measurements, thermoluminescence and lifetime measurements at different wavelengths. This work highlights the critical role that the CaF2 native defects play in the photoluminescence dynamics of Tb3+ ions incorporated in a CaF2 matrix. The sample doped with 10 mol% of Tb3+ ions was found to be stable under prolonged 254 nm ultraviolet irradiation.