Repair of swine full-thickness cutaneous deficiency by autogenic BMSCs compounded with collagen membrane
To supply references to tissue-engineered skin clinical applications with autogenic BMSCs composited collagen membrane to repair swine full-thickness cutaneous deficiency. Twenty mL bone marrow were obtained respectively from 4 swine, autogenic BMSCs were cultured and passed to the 3rd passage. The...
Saved in:
Published in | Zhongguo xiu fu chong jian wai ke za zhi Vol. 23; no. 3; p. 348 |
---|---|
Main Authors | , , , , , |
Format | Journal Article |
Language | Chinese |
Published |
China
01.03.2009
|
Subjects | |
Online Access | Get more information |
Cover
Loading…
Summary: | To supply references to tissue-engineered skin clinical applications with autogenic BMSCs composited collagen membrane to repair swine full-thickness cutaneous deficiency.
Twenty mL bone marrow were obtained respectively from 4 swine, autogenic BMSCs were cultured and passed to the 3rd passage. The fresh bovine tendon treated by means of chemically cross-linked was made 5 cm diameter collagen I (Col I) membrane. The 2 x 10(7)/mL P3 swine autogenic BMSCs labeled DAPI were planted to sterile Col I membrane for 24 hours incubation, then the tissue-engineered skin was constructed. The five full-thickness skin defect of 5 cm diameter was excised to the muscle from forward to backward on the back midline two sides of swine. The tissue-engineered skin were implanted in the experimental group, while Col I membrane was implanted in control group. After 3 and 8 weeks of implantation, the two swine wound surface healing circumstance was observed and further evaluated with histology analysis and TEM. After 3 weeks of imp |
---|---|