핑거조인트가 국산 낙엽송 소경각재의 휨성능에 미치는 영향

• Published in: 목재공학 Vol. 42; no. 3; pp. 301 - 308
• Main Authors: 김윤희, 장상식, Kim, Yun-Hui, Jang, Sang-Sik
• Format: Journal Article
• Language: Korean
• Published: 한국목재공학회 01.05.2014
• Subjects: 임학; standard allowable bending stress; domestic small diameter log; Larix Kaempferi Carr
• ISSN: 1017-0715; 2233-7180

Despite Korea forest take 63.7% of the nation's territory, productivity of domestic structural lumber is low. Studies of domestic small lumbers need to be improved domestic structural timber productivity. In this study, small diameter lumber and finger joint small diameter lumber took bending test to calculate MOE and MOR. MOE of small diameter lumber was $9.3kN/mm^2$ and MOE of finger joint small diameter lumber was $15.4kN/mm^2$. Allowable standard bending stress of small diameter lumber and finger joint small diameter lumber was calculated according to ASTM D 2915. Standard allowable bending stress of small diameter lumber was $12N/mm^2$ and standard allowable bending stress of finger joint small diameter lumber was $11N/mm^2$. Standard allowable bending stress of finger joint small diameter lumber should be considered to design structural beam members. 국토면적의 약 64%가 산림으로 구성되어 OECD 국가 중 네 번째로 산림면적의 비율이 높은 편임에도 원목 생산보다는 녹화에 초점을 맞추어 진행된 조림의 결과로 국내 목재자급률은 약 16.2%에 불구하다. 본 연구에서는 국산 간벌재로부터 소경각재를 생산하여 다중접착을 통해 기둥과 보 등의 다양한 구조용 집성재 제조하기 위하여 핑거조인트가 포함된 소경각재의 휨 성능을 핑거조인트가 없는 소경각재의 휨 성능과 비교하였으며 시험결과를 ASTM D2915에 따라 통계처리를 실시하여 허용응력을 산출하고 상호 비교 평가하였다. 기존의 구조용 집성재 생산라인에서 50 mm 이하의 층재에 대하여 사용하였던 핑거조인트 기계를 사용하여 제조된 핑거조인트 소경각재는 핑거조인트가 없는 부재에 비하여 50% 이하의 휨강도를 나타낸 반면 개선된 핑거조인트 방법을 적용하여 제조된 핑거조인트 부재는 약 80% 정도의 휨강도를 나타내었다. 또한, ASTM D 2915에 따라 핑거조인트가 없는 소경각재 및 핑거조인트가 포함된 소경각재의 허용 휨응력은 각각 12 MPa 및 11.4 MPa로 나타났다. 핑거조인트가 있는 소경각재의 경우에 핑거조인트가 없는 부재보다 강도의 편차가 적었으며, MOR은 약 80% 수준을 나타내었으나 허용 휨응력은 약 95% 수준을 나타내었다.