Nb이 첨가된 Ti합금의 미세 조직 및 산화 거동
The oxidation behavior of Ti-Nb alloys was studied in dry atmosphere. After vacuum arc melting and hot rolling treatment, Ti-Nb alloys were oxidized at $450^{\circ}C$∼$750^{\circ}C$. The oxidation behaviors between matrix and oxide scale were analyzed by SEM, XPS and XRD. Ti-Nb alloys had higher oxi...
Saved in:
Published in | Biuletyn Uniejowski Vol. 37; no. 1; pp. 58 - 63 |
---|---|
Main Authors | , , , , , , |
Format | Journal Article |
Language | Korean |
Published |
한국표면공학회
2004
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | The oxidation behavior of Ti-Nb alloys was studied in dry atmosphere. After vacuum arc melting and hot rolling treatment, Ti-Nb alloys were oxidized at $450^{\circ}C$∼$750^{\circ}C$. The oxidation behaviors between matrix and oxide scale were analyzed by SEM, XPS and XRD. Ti-Nb alloys had higher oxidation resistance than pure Ti at $750^{\circ}C$. XPS analysis of oxide film revealed that $TiO_2$ oxide was formed on the top of surface. The weight gains during the oxidation increase rapidly at temperature above $600^{\circ}C$ which obey the parabolic law. |
---|---|
Bibliography: | KISTI1.1003/JNL.JAKO200411922288220 G704-000261.2004.37.1.004 |
ISSN: | 1225-8024 2299-8403 2288-8403 |