伸線加工および変態時に導入された転位への水素トラップと炭素偏析の競合現象

• Published in: 鉄と鋼 Vol. 100; no. 10; pp. 1322 - 1328
• Main Authors: 平上, 大輔, 山﨑, 真吾, 樽井, 敏三, 潮田, 浩作
• Format: Journal Article
• Language: Japanese
• Published: 一般社団法人 日本鉄鋼協会 2014
• Subjects: delayed fracture; high strength steel; hydrogen analysis; hydrogen embrittlement; hydrogen trapping site
• ISSN: 0021-1575; 1883-2954
• DOI: 10.2355/tetsutohagane.100.1322

Hydrogen embrittlement has become a crucial issue with the promotion of high-strength steel. Many studies have been conducted on the mechanism of hydrogen embrittlement. Because the elucidation of the state of hydrogen is important to understand the mechanism, the states of hydrogen in the steels investigated were controlled. In the present study, 0.35 mass% C and 0.8 mass% C steels annealed in the hydrogen atmosphere followed by quenching from the austenite region together with drawn pearlitic steel of 0.8 mass% C were used to analyze the state of the hydrogen contributing to the emission peak, in particular, at about 300 ºC in the Thermal Desorption Analysis (TDA) curve. The peak at 300 ºC was significant for quenched 0.8 mass% C steel with low Ms temperature; however, the peak decreased with aging at room temperature. However, in 0.35 mass% C steel with high Ms temperature, the peak at 300 ºC was no longer observed. Moreover, in the hydrogen charged as drawn 0.8 mass% pearlitic steel, the peak at 300 ºC did not change with aging at room temperature because of no significant carbon in solid solution, while the peak at 100 ºC decreased with the increase in aging time. Taking into account the competitive phenomenon of hydrogen trapping at the dislocation core and C segregation to dislocations during room temperature aging or during quenching from Ms temperature, it was concluded that the hydrogen peak at about 300 ºC is hydrogen trapped in the dislocation core, while the other hydrogen peak at 100 ºC is attributed to the hydrogen trapped by the stress field generated by dislocation.