COMPARATIVE EVALUATION OF COTTON-LIKE FIBROUS COLLAGEN HEMOSTATS MADE FROM HEAT-DEHYDRATION CROSS -LINKED COLLAGEN
We manufactured four types of cotton-like collagen hemostat which were made from atelocollagen fibers cross-linked by heat dehydration for use as topical hemostatic agents. Their fibers were 1) 15-25μm in diameter, 0.5 cm in length, 2)15-25μm in diameter, 1.0 cm in length, 3) 15-25μ m in diameter, 3...
Saved in:
Published in | Jinko Zoki Vol. 27; no. 1; pp. 262 - 268 |
---|---|
Main Authors | , , , , , , , , |
Format | Journal Article |
Language | Japanese |
Published |
JAPANESE SOCIETY FOR ARTIFICIAL ORGANS
1998
|
Subjects | |
Online Access | Get full text |
Cover
Loading…
Summary: | We manufactured four types of cotton-like collagen hemostat which were made from atelocollagen fibers cross-linked by heat dehydration for use as topical hemostatic agents. Their fibers were 1) 15-25μm in diameter, 0.5 cm in length, 2)15-25μm in diameter, 1.0 cm in length, 3) 15-25μ m in diameter, 3.0 cm in length, and 4) 20-40μm in diameter, 3.0 cm in length. The hemostatic efficacies of these four hemostats were compared with a commercially available collagen hemostat ( Integran®) and oxycellulose ( Oxycel®) in the canine spleen under normal or low blood pressure. It was found that;type 4) and Oxycel® showed complete hemostasis under both normal and low blood pressure, and that Type 3) showed complete hemostasis only under low blood pressure. Type 4) showed higher hemostatic efficiency than Integran®or Oxycel®. The hemostasis rates of our hemostats were higher than those of Oxycel® within 3 min. after attachment of the hemostats. Tissue reaction to these collagen hemostats was minimal at two weeks after implantation. |
---|---|
ISSN: | 0300-0818 1883-6097 |
DOI: | 10.11392/jsao1972.27.262 |