X-Ray Single Crystal Refinement and Superconductivity of La3Ni2B2N3

• Published in: Zeitschrift für anorganische und allgemeine Chemie (1950) Vol. 629; no. 1; pp. 129 - 132
• Main Authors: Blaschkowski, Björn, Meyer, H.-Jürgen
• Format: Journal Article
• Language: English
• Published: Weinheim WILEY-VCH Verlag 01.01.2003; WILEY‐VCH Verlag
• Subjects: Boron; Crystal structure; Lanthanum; Magnetic properties; Nickel; Nitridoborates; Superconductor
• ISSN: 0044-2313; 1521-3749
• DOI: 10.1002/zaac.200390004

Crystalline samples of La3Ni2B2N3 were synthesized using solid state metathesis reactions from combinations of La, LaCl3, NiCl2 together with Li3BN2. The structure was determined by single crystal X‐ray diffraction (I4/mmm (No. 139), a = 372.95(2) pm, c = 2056.3(2) pm, R1 = 0.027, wR2 = 0.062) and confirmed earlier results from neutron powder diffraction. La3Ni2B2N3 contains BN units capping square planar Ni layers. Isolated nitrogen atoms reside in La6 octahedra. Magnetic measurements on several bulk samples exhibit superconductivity at temperatures below 14.6 K. Einkristall‐Röntgenstrukturanalyse und Supraleitung von La3Ni2B2N3 Kristalline Proben von La3Ni2B2N3 wurden durch Festkörper‐Metathese‐Reaktionen aus Kombinationen von La, LaCl3, NiCl2 zusammen mit Li3BN2 erhalten. Die durchgeführte Einkristall‐Röntgenstrukturuntersuchung (I4/mmm (No. 139), a = 372.95(2) pm, c = 2056.3(2) pm, R1 = 0.027, wR2 = 0.062) bestätigt eine frühere Pulver‐Neutronenbeugungsuntersuchung. La3Ni2B2N3 enthält BN‐Einheiten, welche quadratisch‐planare Ni‐Schichten überdachen sowie isolierte N‐Atome in La6‐Oktaedern. Magnetische Messungen an verschiedenen Proben zeigen supraleitendes Verhalten unterhalb 14.6 K.