A New Mechanism of Poly-silicon Crater Defect Induced from Al Tiny Particle Charging Effect during Water Rinse in Oxide Patterning Process

Poly-silicon crater defect generated in large plate of n+ poly-silicon on p-type substrate that resulted in gate oxide integrity (GOI) failure in 0.15mum silicon process is investigated. Al tiny particle accidentally introduced from PECVD resistance protection oxide (RPO) deposition is found to be a...

Full description

Saved in:
Bibliographic Details
Published in2006 IEEE International Integrated Reliability Workshop Final Report pp. 198 - 200
Main Authors Duan, L.J., Au, H.H., Kuan, M., Quek, P.S., Pey, K.S.
Format Conference Proceeding
LanguageEnglish
Published IEEE 01.10.2006
Subjects
Al tiny particle
Capacitance
charging
Corrosion
DI water rinse
diluted HF immersion
galvanic corrosion
Galvanizing
GOI failure
Particle charging
Poly-silicon crater defect
Protection
Silicon
Spinning
Testing
Water storage
Wet etching
Online AccessGet full text

Cover

More Information
Summary:Poly-silicon crater defect generated in large plate of n+ poly-silicon on p-type substrate that resulted in gate oxide integrity (GOI) failure in 0.15mum silicon process is investigated. Al tiny particle accidentally introduced from PECVD resistance protection oxide (RPO) deposition is found to be able to translate into such poly-silicon crater defect in the test structure during subsequent oxide photo-resist patterning and oxide wet etching. The defect size can correlate to DI water rinse time of photo-resist developing in RPO oxide patterning. The longer time of water rinse, the larger size of the craters. This paper describes observation of n+ poly-silicon crater formation. A new mechanism of Al tiny particle induced n+ poly-silicon charging effect during high speed spinning water rinse in oxide patterning process is proposed. After water rinse completion in the process, the charges stored in poly-silicon are unable to be discharged immediately due to enough large capacitance of gate oxide in discharging path of the test structure. Charged poly-silicon is then quickly attacked in diluted 0.5w%HF immersion of RPO oxide wet etching by galvanic corrosion to form a crater. To eliminate poly-silicon crater formation, efforts could be put into eliminating the presence of aluminum particles in oxide deposition or optimization of water rinse condition. Oxide dry etching is also one of possible improvements can be evaluated
ISBN:1424402964
9781424402960
ISSN:1930-8841
2374-8036
DOI:10.1109/IRWS.2006.305245